Formulation of the Effect of Different Alloying Elements on the Tensile Strength of the in situ Al-Mg2Si Composites
نویسندگان
چکیده
In this paper, the effect of different alloying elements on the ultimate tensile strength of Al-Mg2Si composites is theoretically studied. The feed forward back propagation neural network with sigmoid function is used. The extensive experimental results taken from literature are modeled and mathematical formula is presented in explicit form. In addition, it is observed that magnesium and copper have a stronger effect on the ultimate tensile strength of Al-Mg2Si composites comparison to other alloying elements. The proposed model shows good agreement with test results and can be used to find the ultimate tensile strength of Al-Mg2Si composites.
منابع مشابه
IN SITU FABRICATION OF Al 2024-Mg2Si COMPOSITE BY SPARK PLASMA SINTERING OF REACTIVE MECHANICALLY ALLOYED POWDER
In situ Al2024- Mg2Si composite was fabricated by spark plasma sintering (SPS) of reactive powder. Reactive powder was obtained from mechanical alloying (MA) of elemental powders. Clad layers of in situ composite were fabricated on Al substrates by spark plasma sintering (SPS). Structural evolution during MA process and after SPS was investigated by X-ray diffractometery (XRD). Scanning electro...
متن کاملHigh Temperature Properties of AZ91D Magnesium Alloy Composite Reinforced with Short Alumina Fiber and Mg_{2}Si Particle
Short alumina fiberand in situ Mg2Si particle reinforced magnesium alloy composites were fabricated by squeeze casting. The in situ Mg2Si particles were formed during the infiltration with the melt into the preforms consisting of the fibers having Si particles attached to their surfaces. The microstructure of the composites and their tensile strength and Young’s modulus in the range from 293K t...
متن کاملEffect of Particle Size on the Structural and Mechanical Properties of Al–AlN Nanocomposites Fabricated by Mechanical Alloying
Nanostructured Al composites with 2.5 wt.% aluminum nitride (AlN) were fabricated by powder metallurgy using mechanically milled aluminum powder mixed in a planetary ball mill with different particle sizes of AlN (50 nm and 1 μm) as reinforcement. After 20 h milling, the powders were die-pressed uniaxially in a steel die and then sintered at 670 °C for 2 h. The morphologies and properties of th...
متن کاملMagnificent Grain Refinement of Al-Mg2Si Composite by Hot Rolling
The effect of chemical composition and the hot rolling operations on the microstructure and mechanical properties of in situ aluminum matrix composite with Mg2Si phase as the reinforcement was studied. It was revealed that the modification by phosphorous results in the rounder (more spherical) primary and secondary (eutectic) magnesium silicide intermetallics. During hot rolling, the primary pa...
متن کاملتأثیر افزودن جوانهزای Al-5Ti-B بر درجهبندی ریزساختار استوانه ریخته شده از کامپوزیت Al-13.8 wt.% Mg2Si بهروش ریختهگری گریز از مرکز
To evaluate the effect of inoculant addition on functionally graded microstructure of centrifugally cast Al-Mg2Si composites, two cylinders of Al-13.8 wt.% Mg2Si with and without the addition of 1 wt.% Al-5Ti-B inoculant were cast in a vertical centrifugal casting machine. The chemical composition, microstructures and microstructural phases of the different radial sections of the cast cylinders...
متن کامل