Thermionic emission from phosphorus (P) doped diamond nanocrystals supported by conical carbon nanotubes and ultraviolet photoelectron spectroscopy study of P-doped diamond films
نویسندگان
چکیده
a Department of Physics and Astronomy, University of Louisville, Louisville 40292, KY, United States b Department of Materials Science & Engineering, Iowa State University, Ames 50011, IA, United States c Department of Chemical Engineering, University of Louisville, Louisville 40292, KY, United States d Conn Center for Renewable Energy Research, University of Louisville, Louisville 40292, KY, United States e Electro-Optics Research Institute & Nanotechnology Center, University of Louisville, Louisville 40292, KY, United States
منابع مشابه
Solid-State and Vacuum Thermionic Energy Conversion
A brief overview of the research activities at the Thermionic Energy Conversion (TEC) Center is given. The goal is to achieve direct thermal to electric energy conversion with >20% efficiency and >1W/cm power density at a hot side temperature of 300-650C. Thermionic emission in both vacuum and solid-state devices is investigated. In the case of solid-state devices, hot electron filtering using ...
متن کاملInvestigation of structure, adhesion strength, wear performance and corrosion behavior of platinum/ruthenium/nitrogen doped diamond-like carbon thin films with respect to film thickness
In this study, the corrosion performance of platinum/ruthenium/nitrogen doped diamond-like carbon (PtRuN-DLC) thin films deposited on p-Si substrates using a DCmagnetron sputtering deposition system in a 0.1M NaCl solution was investigated using potentiodynamic polarization test in terms of film thickness. Theeffect of thefilmthickness on the chemical composition, bonding structure, surfacemorp...
متن کاملStructure, adhesive strength and electrochemical performance of nitrogen doped diamond-like carbon thin films deposited via DC magnetron sputtering.
Nitrogen doped diamond-like carbon (DLC:N) thin films were deposited on p-Si (100) substrates by DC magnetron sputtering with different nitrogen flow rates at a substrate temperature of about 100 degrees C. The chemical bonding structure of the films was characterized by X-ray photoelectron spectroscopy (XPS) and micro-Raman spectroscopy. The adhesive strength and surface morphology of the film...
متن کاملNitrogen-Induced Degradation of Corrosion Resistance of Platinum/Ruthenium/Nitrogen-Doped Diamond-like Carbon Thin Films
An influence of nitrogen incorporation on the chemical composition, bonding structure, surface morphology and activity, adhesion strength, and corrosion resistance of platinum/ruthenium/nitrogen-doped diamond-like carbon PtRuN-DLC thin films deposited on conductive p-Si 100 substrates using dc magnetron sputtering deposition was investigated using X-ray photoelectron spectroscopy, micro-Raman s...
متن کاملDirect electrochemical response of glucose at nickel-doped diamond like carbon thin film electrodes
Ni-doped diamond like carbon (NiDLC) thin films were deposited on Si substrates by cosputtering a pure Ni target with different DC powers (10, 20, 30, and 40 W) and a pure graphite target with a DC power of about 650 W at room temperature. X-ray photoelectron spectroscopy (XPS) was used to measure the chemical composition and binding energy of the NiDLC thin films, and the C bonding structures ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2014