Department of Physics and Astronomy, Rice University, Houston, TX 77005, USA. Na tional High Magnetic Field Laboratory, Florida State University, Tallahassee, FL 32310 USA. Department of Mechanical Engineering, Texas A&M University, College Station TX 77843, USA. Materials Science and NanoEngineering, Rice University, Houston, TX 77005, USA. Department of Translational Molecular Pathology, University of Texa MD Anderson Cancer Center, Houston, TX 77005, USA. *Corresponding author. Email: [email protected]
منابع مشابه
High hardness in the biocompatible intermetallic compound β-Ti3Au
The search for new hard materials is often challenging, but strongly motivated by the vast application potential such materials hold. Ti3Au exhibits high hardness values (about four times those of pure Ti and most steel alloys), reduced coefficient of friction and wear rates, and biocompatibility, all of which are optimal traits for orthopedic, dental, and prosthetic applications. In addition, ...
متن کاملCross-sectional TEM analysis of porcelain fused to gold-coated titanium.
This study investigated the interfacial microstructure between gold-coated titanium and low-fusing porcelain. The square surfaces of cast titanium split rods were sputter-coated with gold using a sputter coater at 40 mA for 1,000 seconds. Specimens were prepared for transmission electron microscopy (TEM) by cutting and polishing two pieces of the gold-coated split-rod specimens, which were glue...
متن کاملOn the microstrctral and machanical properties of similar TLP bonding of Inconel 600 superalloy sheet
In this study, microstructural evaluation and mechanical properties of similar TLP bonded of Inconel 600 by using of BNi-2 interlayer were investigated. The bonding tests were carried out at 1050°C and 1100°C for 5-45 min which homogenization treatment was performed on the best of the bonded samples. Results showed that Ni-B eutectic compound was formed in the a-thermally solidification zone (A...
متن کاملOn the microstrctral and machanical properties of similar TLP bonding of Inconel 600 superalloy sheet
In this study, microstructural evaluation and mechanical properties of similar TLP bonded of Inconel 600 by using of BNi-2 interlayer were investigated. The bonding tests were carried out at 1050°C and 1100°C for 5-45 min which homogenization treatment was performed on the best of the bonded samples. Results showed that Ni-B eutectic compound was formed in the a-thermally solidification zone (A...
متن کاملInvestigating the Joining of Ni3Al Intermetallic Compound, using Transient Liquid Phase (TLP) Method with Cu Interlayer
In this study, joining of Ni3Al intermetallic compounds using the transient liquid phase (TLP) process with Cu interlayer was investigated. The binding process was carried out in a vacuum furnace at a temperature of 1050 °C for different times of 30, 60, 90 and 120 minutes. The effect of time variation on microstructure and mechanical properties of the joint zone was investigated. The EDS analy...