Crystal orientation-ordered ZnS nanobelt quasi-arrays and their enhanced field-emission.
نویسندگان
چکیده
Crystal orientation-ordered ZnS nanobelt quasi-arrays were fabricated using a non-catalytic and template-free thermal evaporation process; field-emission measurements show that these novel arrays are decent field emitters possessing a current density more than 20 times higher than that of randomly-oriented ZnS nanobelt ensembles at a macroscopic field of 5.5 V microm(-1).
منابع مشابه
Fabrication of TaS2 nanobelt arrays and their enhanced field-emission.
Crystal TaS2 nanobelt arrays were fabricated on Ta wafers by a two-step method. Field-emission measurements show that the nanobelt arrays are decent field emitters with a turn-on field of approximately 0.7 V microm(-1), a threshold field of approximately 2.1 V microm(-1), and a field enhancement factor of approximately 4.33 x 10(4).
متن کاملCrystal orientation-ordered ZnS nanowire bundles.
We report a novel approach for growing aligned and orientation-ordered ZnS nanowires. Our method relies on a buffer layer of CdSe grown on a Si(111) substrate, on which ZnS nanowires are grown. The growth process of the nanowire bundles is presented. The technique demonstrated could be an effective pathway for growing patterned, aligned, size-controlled, and orientation-ordered ZnS nanowires.
متن کاملDense and vertically-aligned centimetre-long ZnS nanowire arrays: ionic liquid assisted synthesis and their field emission properties.
Based on the self-ordering behavior of ionic liquids on solid surface, a gold ion containing ionic liquid was employed to obtain a uniform pattern of gold nanoparticles on Si substrate. Using this catalytic pattern, super-dense, centimetre long, well-crystallized and vertically-aligned ZnS nanowire arrays were then generated. It was found that the densely-packed gold nanoparticles played a key ...
متن کاملOrdered arrays of tilted silicon nanobelts with enhanced solar hydrogen evolution performance.
Well-ordered tilted silicon nanobelt arrays have been fabricated over a large area (≥2.5 cm(2)) by metal assisted chemical etching of pre-patterned silicon, which demonstrated markedly enhanced solar hydrogen evolution performance, compared with planar silicon of the same type and previously reported silicon nanowires prepared in a similar way.
متن کاملZnO-ZnS heterojunction and ZnS nanowire arrays for electricity generation.
Vertically aligned ZnO-ZnS heterojunction nanowire (NW) arrays were synthesized by thermal evaporation in a tube furnace under controlled conditions. Both ZnO and ZnS are of wurtzite structure, and the axial heterojunctions are formed by epitaxial growth of ZnO on ZnS with an orientation relationship of [0001](ZnO)//[0001](ZnS). Vertical ZnS NW arrays have been obtained by selectively etching Z...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 29 شماره
صفحات -
تاریخ انتشار 2007