The effect of fired scrap addition on the sintering behaviour of hard porcelain
نویسندگان
چکیده
The effect of the addition of porcelain fired scraps on the sintering, phase composition and properties of a hard porcelain was studied. Two ceramics were compared: a commercial triaxial porcelain labelled C-0 and one, where 15% of the mass of C-0 was substituted by scraps yielding a composition labelled C-15. The sintering was evaluated by the linear shrinkage, the water absorption and the variation of closed and total porosity, while the phase transformations were investigated by DTA-TG, dilatometry and XRD. Samples, sintered at 1350 and 1400 8C, were used for the evaluation of the Young modulus and the bending strength. The addition of the fired scrap had a positive effect on the quartz dissolution and on the formation of the liquid phase during the sintering. The sintering and the mechanical properties were improved by heat treatment in the 1300–1350 8C range. Above this temperature, a significant over-firing with a decrease of the mechanical properties was observed. # 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
منابع مشابه
Evaluation of Heterogeneous Densification, Anisotropic Shrinkage and Rheological Behavior of Ceramic Materials during Liquid Phase Sintering by Numerical-Experimental Procedure
The effective shear and bulk viscosity, as well as dynamic viscosity, describe the rheological properties of the ceramic body during the liquid phase sintering process. The rheological parameters depend on the physical and thermo-mechanical characteristics of the material such as relative density, temperature, grain size, diffusion coefficient, and activation energy. Thermal behavior of the cer...
متن کاملEffect of Core Thickness and Porcelain Sintering on Marginal Adaptation
Background and aim: Marginal adaptation affects the long-term success of full-coverage restorations. This study aimed to assess the effect of porcelain sintering and zirconia core thickness on the marginal adaptation of all-ceramic restorations. Materials and methods: In this in-vitro experimental study, a standard brass die, 7 mm in length and 5 mm in diameter, was fabricated using a milling ...
متن کاملEffect of Nano and Micro Silica on the pyroplastic deformation of Domestic porcelain tile
The term " pyroplasticity" refers to the deformation of the white ware that occurs during firing. In particular, this phenomenon is particularly important for tiles fired in roller kiln (especially thin and large dimensions) and the roughness created on the surface by vertical weight. In this study, 1, 3 and 5% of nanosilica and microsilica were replaced in porcelain tile batch. The effect of n...
متن کاملبررسی اثر پخت مکرر پرسلن بر مقاومت باند در دو نوع آلیاژ بیس متال (مینالوکس و وراباند 2)
The formation of oxides on the surface of the metal are proven to contribute to the formation of strong bonding. However, The base metal alloys are expected to exhibit more oxidation than high gold alloys, increase in oxide layer thickness due to repeated firing in them can reduce the bond strength. The aim of this study was to compare the effect of repeated porcelain firing on the bond strengt...
متن کاملSynthesis and Characterization of Porcelain Body Developed from Rice Husk Ash (TECHNICAL NOTE)
For a developing country like Bangladesh, waste management is an important issue. Since it is a small over-populated country , strict government regulations regarding landfills is essential. Expansion of ceramic industries is considered to be one of the potential sectors for the economic growth of Bangladesh. However, raw material cost per unit production is the prime concern for industrialists...
متن کامل