An in vitro investigation of wear resistance and hardness of composite resins.

PURPOSE The aim of the present study was to investigate the wear resistance and hardness of five kinds of composite resins. MATERIALS AND METHODS Sixty-five specimens were fabricated with one nano-hybrid (Charisma Diamond), two micro-hybrid (3MZ250, Clearfil AP-X) and two packable (3MP60, Surefil) composite resins, according to a randomized complete block design (n=13, 8 for wear test; 5 for hardness test). The composites were filled in a rectangular mold, and light polymerization. After storage in 37°C deionized water for 24h, all specimens were tested with a custom-made toothbrush machine with a stainless-steel ball as antagonist (3N loads, 1Hz, 6×10(5) cycles) immersed in calcium fluoride slurry. Wear volume, hardness and surface structure of each tested material was examined by a three-dimensional non-contact optical profilometer, Vickers indentation technique and scanning electron microscope. RESULTS The volume loss ranked from least to most as follows: Charisma Diamond, P60, Z250, Clearfil AP-X and Surefil. Regarding hardness, the rank from highest to lowest as follows: Clearfil AP-X, P60, Surefil, Z250, Charisma Diamond. The interactions between wear resistance and microhardness were not significant. CONCLUSIONS The custom-made machine is considered suitable to simulate sliding of an antagonist cusp on an opposing occlusal composite restoration. Nanofilled composite may have superior wear compared to other composite resins.