COERCIVITY MECHANISM OF MELT-SPUN Sm(Fel1Ti)
نویسندگان
چکیده
Hysteresis loops of randomly oriented grains with uniaxial anisotropy were computed on the basis of an array of 27 Wigner Seitz cells representing crystallites which interact by exchange coupling at the grain boundaries. The computed coercivity increases linearly with increasing interatomic exchange. Using the experimental anisotropy and exchange parameters for Sm(FellTi), we found 1.lo&=1.2 T in good agreement with results on melt-spun ribbon. The main insight is that strong intergrain coupling is beneficial for developing coercivity in nanocrystalline alloys with uniaxial anisotropy.
منابع مشابه
Coercivity Mechanism of (Nd0.8Ce0.2)2.4Fe12Co2B Ribbons with Ferromagnetic Grain Boundary Phase
Understanding the coercivity mechanism has had a substantial impact on developing economically more attractive RE-based (RE = rare earth) permanent materials because of price volatility of key RE metals (i.e., Nd and Dy) in recent years. In this work, we investigated the microstructure and magnetic properties of melt-spun (Nd0.8Ce0.2)2.4Fe12Co₂B ribbons and annealed samples at 773 K for 15 min ...
متن کاملThe Structure and Magnetic Properties of Co77Zr18W5 Melt-Spun Ribbons
Based on X-ray diffraction, microscopic and magnetic analysis, the structure and magnetic properties of Co77Zr18W5 melt-spun ribbons were studied in this paper. A new element to stabilize the metastable Co5Zr phase was found and the coercivity observed in Co-Zr alloys can be obviously enhanced by proper tungsten substitution. The Curie temperature of Co77Zr18W5 ribbons is 475 ̊C which suggests t...
متن کاملEffect of Sm content on energy product of rapidly quenched and oriented SmCo5 ribbons
The Sm-content dependence of phase composition, anisotropy, and other magnetic properties of Sm1+δCo5 (δ ≤ 0.12) ribbons melt spun at 10 m/s has been studied. The samples consist of hexagonal SmCo5 grains whose c axes are preferentially aligned along the long direction of the ribbon. The lattice parameter a and the cell volume (V) increase with increasing Sm content δ, whereas c decreases. Sm a...
متن کاملEffects of annealing on the coercivity of Sm(Co,Fe,Cu,Zr)z ribbons and its temperature dependence
Sm(CobalFe0.1CuxZr0.03)7 (x = 0.0–0.25) ribbons have been prepared by melt spinning. The effects of annealing parameters on coercivity and its temperature dependence have been studied systematically. It is found that the melt-spinning technique remarkably improves the magnetic properties and simplifies the annealing process. The high-performance precipitation-hardened magnets can be obtained by...
متن کاملDirectional annealing-induced texture in melt-spun (Sm12Co88)99Nb1 alloy
Developing texture in nanocrystalline permanent magnet alloys is of significant importance. Directional annealing is shown to produce texture in the permanent magnet alloy (Sm12Co88)99Nb1. Melt spinning produced isotropic grain structures of the hard magnetic metastable SmCo7 phase, with grain sizes of ∼300 nm. Conventional annealing of melt-spun (Sm12Co88)99Nb1 alloy produced Sm2Co17 phase wit...
متن کامل