Mechanically stable, hierarchically porous Cu3(btc)2 (HKUST-1) monoliths via direct conversion of copper(II) hydroxide-based monoliths.
نویسندگان
چکیده
The synthesis of highly crystalline macro-meso-microporous monolithic Cu3(btc)2 (HKUST-1; btc(3-) = benzene-1,3,5-tricarboxylate) is demonstrated by direct conversion of Cu(OH)2-based monoliths while preserving the characteristic macroporous structure. The high mechanical strength of the monoliths is promising for possible applications to continuous flow reactors.
منابع مشابه
Synthesis of Porous Carbon Monoliths Using Hard Templates
The preparation of porous carbon monoliths with a defined shape via template-assisted routes is reported. Monoliths made from porous concrete and zeolite were each used as the template. The porous concrete-derived carbon monoliths exhibited high gravimetric specific surface areas up to 2000 m²·g-1. The pore system comprised macro-, meso-, and micropores. These pores were hierarchically arranged...
متن کاملSynthesis of Different Copper Oxide Nano-Structures From Direct Thermal Decomposition of Porous Copper(ΙΙ) Metal-Organic Framework Precursors
Copper oxide nanostructures have been successfully synthesized via one-step solid-state thermolysis of two metal-organic frameworks, [Cu3(btc)2] (1) and [Cu(tpa).(dmf)] (2), (btc = benzene-1,3,5-tricarboxylate, tpa = therephtalic acid = 1,4-benzendicarboxylic acid and dmf = dimethyl formamide) under air atmosphere at 400, 500, and 600°C. It has also been found that the reaction temperature pla...
متن کاملStructurally designed synthesis of mechanically stable poly(benzoxazine-co-resol)-based porous carbon monoliths and their application as high-performance CO2 capture sorbents.
Porous carbon monoliths with defined multilength scale pore structures, a nitrogen-containing framework, and high mechanical strength were synthesized through a self-assembly of poly(benzoxazine-co-resol) and a carbonization process. Importantly, this synthesis can be easily scaled up to prepare carbon monoliths with identical pore structures. By controlling the reaction conditions, porous carb...
متن کاملAligned macroporous monoliths with intrinsic microporosity via a frozen-solvent-templating approach.
Aligned macroporous monoliths of an organic cage, a polymer of intrinsic microporosity (PIM-1), and a metal-organic framework (HKUST-1) are prepared by a controlled freezing approach. In addition to macropores, all the monoliths contain the intrinsic micropores.
متن کاملHierarchically porous carbon monoliths with high surface area from bridged polysilsesquioxanes without thermal activation process.
Hierarchically porous carbon monoliths with high specific surface areas have been fabricated by removing nano-sized silica phase from carbon/silica composites pyrolyzed from bridged polysilsesquioxane. This activation method improves the homogeneity between inner and outer parts of the monoliths compared to the conventional thermal activation methods.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 51 17 شماره
صفحات -
تاریخ انتشار 2015