Comparative evaluation of chlorhexidine, grape seed extract, riboflavin/chitosan modification on microtensile bond strength of composite resin to dentin after polymerase chain reaction thermocycling: An in vitro study
نویسندگان
چکیده
AIM The purpose of this study was to evaluate the influence of chlorhexidine (CHX), grape seed extract (GSE), riboflavin/chitosan modification on microtensile bond strength (μTBS) of composite resin to dentin after polymerase chain reaction (PCR) thermocycling. MATERIALS AND METHODS Forty extracted human molars were used and a flat surface was then prepared by removing the occlusal one-third. The teeth were randomly assigned into four groups - Group I in which self-etch adhesive (Adper Easy One) was applied and Groups II, III, IV were pretreated with 2% CHX, 6.5% GSE, and 1% riboflavin/chitosan, respectively, before the application of self-etch adhesive. Composite build-ups were constructed, and PCR thermocycling (5000 cycles) was performed. The μTBS was evaluated using the universal testing machine. Data were analyzed using one-way analysis of variance and Tukey's test. RESULTS The mean μTBS values for Group I (control), Group II (CHX), Group III (GSE), and Group IV (riboflavin/chitosan modification) were 30.81, 43.15, 38.79, and 35.07 MPa, respectively. CONCLUSION Pretreatment with CHX and GSE leads to a significant increase in μTBS of composite resin to dentin.
منابع مشابه
Effect of triple Antibiotic paste and 2% chlorhexidine gel on shear bond strength of composite resin to dentin; an in vitro study
متن کامل
Micro-Shear Bond Strength of Indirect Composite Resin to Three Different Computer-Milled Cores After Thermocycling
Background and Aim: The aim of this study was to evaluate the micro-shear bond strength of an indirect composite resin to three different types of cores. Materials and Methods: In this in-vitro study, 14 blocks (5×5×2 mm) were designed and milled by computer from cobalt-chromium (Co-Cr) alloy, zirconia, and polyether ether ketone (PEEK). Each sample was treated according to the manufacturer’s ...
متن کاملEvaluation of microtensile bond strength of repaired dental resin composite using different surface treatment techniques: A laboratory study
Background and Aims: Today, resin composites are one of the most commonly used materials in restorative dentistry. However, failure in resin treatments is also common due to its chemical nature and its high talent for decay recurrence. According to conservative approaches, "conservative" treatments are more likely to be considered than "Replacement" of damaged remedies. The purpose of this stud...
متن کاملEffect of chlorhexidine application on the bond strength of resin core to axial dentin in endodontic cavity
OBJECTIVES This study evaluated the influence of chlorhexidine (CHX) on the microtensile bonds strength (µTBS) of resin core with two adhesive systems to dentin in endodontic cavities. MATERIALS AND METHODS Flat dentinal surfaces in 40 molar endodontic cavities were treated with self-etch adhesive system, Contax (DMG) and total-etch adhesive system, Adper Single Bond 2 (3M ESPE) after the fol...
متن کاملEffect of Er: YAG laser, diamond bur and sandblasting on the microtensile bond strength of the composite to noncarious cervical lesions
Background and Aims: Restoration of non-carious cervical lesions (NCCLs) is challenging due to the difficulty of adhesion of dental tissues. The aim of this study was to investigate the effects of three methods of surface treatments using diamond bur, Er: YAG laser and sandblasting on the microtensile bond strength of resin composite to the noncarious dentin in cervical lesions. Materials and ...
متن کامل