PRESSURE EFFECT ON CURIE TEMPERATURE FOR Co1-xBx AMORPHOUS ALLOYS
نویسندگان
چکیده
Pressure effect on Curie temperature, dTc/dp, for amorphous Col-,B, alloys is estimated indirectly from forced volume magnetostriction even in Tc > Tcry. Results estimated indirectly show smaller values compared with those measured directly, and are consistent with thermal expansion. The value of dTc/dp extrapolated to Co agrees with that for crystalline Co.
منابع مشابه
Composition dependence of field induced anisotropy in ferromagnetic „Co,Fe...89Zr7B4 and „Co,Fe...88Zr7B4Cu1 amorphous and nanocrystalline ribbons
The composition dependence of field induced anisotropy KU of field annealed soft ferromagnetic Co1−xFex 89Zr7B4 and Co1−xFex 88Zr7B4Cu1 amorphous and amorphous/nanocrystalline “nanocomposite” melt spun ribbons is investigated. With the exception of the highest Co-containing alloys x 0.10 , the observations are discussed in terms of a superposition of directional pair ordering of Fe,Co atoms and...
متن کاملHigh pressure magnetic behaviour of amorphous YxNi1-x alloys
High pressure magnetization and Curie temperature measurements have been performed on several amorphous Y,Ni,-, alloys. The results seem to indicate that ferromagnetism disappears in a rather inhomogeneous way.
متن کاملMAGNETIC PROPERTIES OF AMORPHOUS Fe-Ti ALLOYS PRODUCED BY FACING TARGET TYPE SPUTTERING
In bulk FeTi alloys prepared by facing target type sputtering, an amorphous phase was obtained between 25 and 75 at% Ti. These alloys are weak itinerant electron ferromagnets and the Curie temperature decreases with increasing Ti concentration and becomes zero at about 60 at% Ti.
متن کاملEffect of minor Co additions on the crystallization and magnetic properties of Fe(Co)NbBCu alloys
The effect of partial replacement of Fe by Co (up to 8 %) on thermal stability, structure and magnetic properties of FeNbBCu alloys has been explored in this paper. The results indicate that Co reduces the stability against crystallization of the amorphous alloy and stabilizes the nanocrystalline phase prior to the further precipitation of metastable boride phases. Transmission Mössbauer spectr...
متن کاملMagnetic Properties of Pr–Fe–Al Alloys Produced by the Metallic Mold Casting Method
The structures and magnetic properties of Pr–Fe–Al alloys produced by the metallic mold casting method were investigated. The Pr–Fe–Al alloy consisted of the amorphous phase together with the non-ferromagnetic Pr phase. Magnetic measurements confirmed that the origin of coercivity in the alloys was the amorphous phase. It was found that the Curie temperature and coercivity of the alloys were st...