Preparation and Characteraction of New Magnetic Co–Al HTLc/Fe3O4Solid Base
نویسندگان
چکیده
Novel magnetic hydrotalcite-like compounds (HTLcs) were synthesized through introducing magnetic substrates (Fe3O4) into the Co–Al HTLcs materials by hydrothermal method. The magnetic Co–Al HTLcs with different Fe3O4 contents were characterized in detail by XRD, FT-IR, SEM, TEM, DSC, and VSM techniques. It has been found that the magnetic substrates were incorporated with HTLcs successfully, although the addition of Fe3O4 might hinder the growth rate of the crystal nucleus. The morphology of the samples showed the relatively uniform hexagonal platelet-like sheets. The grain boundaries were well defined with narrow size distribution. Moreover, the Co–Al HTLcs doped with magnetic substrates presented the paramagnetic property.
منابع مشابه
Preparation and Characterization of a Molybdenum(VI) Schiff Base Complex as Magnetic Nanocatalyst for Synthesis of 2-Amino-4H-benzo[h]chromenes
A new recoverable molybdenum nanocatalyst was prepared by immobilization of a Schiff base ligand on the surface of silica coated magnetite nanoparticles (Fe3O4@SiO2) through condensation reaction between 3-aminopropyl triethoxysilane and 2-hydroxy1-naphthaldehyde and succeeding reaction with dioxomolybdenum(VI) acetylacetonate (MoO2(acac)2). The synthesized cat...
متن کاملSpinel-Type Cobalt Oxide (Co3O4) Nanoparticles from the mer- Co(NH3)3(NO2)3 Complex: Preparation, Characterization, and Study of Optical and Magnetic Properties
In this paper, the mer-Co(NH3)3(NO2)3 complex was used as a new precursor for synthesizing spinel-type cobalt oxide nanoparticles (Co3O4NPs).Thermal decomposition of the complex at low temperature (175 °C) resulted in the Co3O4NPs without using expensive and toxic solvents or complicated equipment. XRD, FT-IR, SEM, EDX, and TEM were employed to characterize the product, and its optical and magn...
متن کاملMagnetic amine-functionalized graphene oxide as a novel and recyclable bifunctional nanocatalyst for solvent-free synthesis of pyrano[3,2-c]pyridine derivatives
The new magnetic amine-functionalized graphene oxide (Fe3O4-GO-NH2) nanocatalyst was prepared through the reaction of 3-aminopropyltriethoxysilane (APTES) with magnetic graphene oxide (Fe3O4-GO). It was characterized by XRD, TEM, SEM, FT-IR and EDX techniques. The intrinsic carboxylic acids on the edges of Fe3O4-GO alo...
متن کاملPreparation and Characterization of Manganese Ferrite Nanoparticles via Co-precipitation Method for Hyperthermia
In this work, Mn ferrite nanopowders were prepared by co-precipitation method and were characterized. Phase identification of the nanopowders was performed by X-ray diffraction method and the mean particle size of the nanopowders was calculated by Scherrer's formula, using necessary corrections. Magnetic parameters of the prepared nanopowders were measured by a vibrating sample magnetome...
متن کاملApplying a suitable route for preparation Fe3O4 nanoparticles by Ammonia and investigation of their physical and different magnetic properties
Iron oxide nanoparticles were synthesized by coprecipitation method using ammonia as precipitation agent. Most researchers usually add ammonia into the iron salt solution but in this work the salt solution drop wise has been added to the ammonia and the new obtained results were compared with those of other researches. Magnetic properties of nanoparticles were measured by VSM. The effect of rea...
متن کامل