Preparation and optical properties of transparent Ce:YAG ceramics for high power white LED
نویسندگان
چکیده
Transparent Ce:YAG ceramics were synthesized from the Ce:YAG powder which was produced by co-preparation method of the hydroxides. The Ce:YAG ceramics exhibit a broad emission band peaked at 530 nm due to the 5d→4f transition of Ce 3+ . The transmittances of the samples obtained were 70 ~ 87 % at 800 nm. The absorption coefficient and emission intensity of Ce 3+ were increased with the increase of the thickness. With increasing thickness of the sample, the color coordinates of the Ce:YAG ceramics under 465 nm LED excitation shifted from the blue region to the yellow region with passing nearby the theoretical white point. The highest value of luminous efficacy of the white LED was 73.5 lm/W.
منابع مشابه
The Role of Factors Influencing the Optical Properties of Yttrium Aluminum Garnet Ceramic Body
Yttrium Aluminum Garnet (Y3Al5O12) is a transparent ceramic with a wide range of applications such as high mechanical strength windows, high power laser sources and radiation detectors. The most important challenge in making these ceramics is the problem of low light transmittance, especially in the visible area in the range of 400 to 700 nm, which is greatly affected and reduced by various fac...
متن کاملCrystallization Kinetics and Characterization of Nanostructure Mica Glass-Ceramics with Optical Transparency
Transparent glasses in a system of Li2O-MgO-SiO2-Al2O3-Fchemical constituents were prepared by melt quenching method. In the fabrication of nanocrystal glass-ceramics, controlled nucleation and subsequent crystal growth were necessary to avoid loss of transparency. It was therefore important to understand thermal properties and crystallization kinetic...
متن کاملThe Effect of Different Solutions on Optical Behavior of Polished and Glazed Zirconia-Reinforced Lithium Silicate Ceramics
Background: This study sought to assess the effect of glazing and polishing surface treatments on the optical behavior of zirconia-reinforced lithium silicate ceramics thermocycled in different solutions. Methods:Computer-aided design/computer-aided manufacturing ceramics (VITA Suprinity) were cut into samples (n=104) measuring 1.5x14x10 mm according to t...
متن کاملTransparent Glass-Ceramics Produced by Sol-Gel: A Suitable Alternative for Photonic Materials
Transparent glass-ceramics have shown interesting optical properties for several photonic applications. In particular, compositions based on oxide glass matrices with fluoride crystals embedded inside, known as oxyfluoride glass-ceramics, have gained increasing interest in the last few decades. Melt-quenching is still the most used method to prepare these materials but sol-gel has been indicate...
متن کاملIn-situ Fabrication of Transparent Magnesium Aluminate Spinel by Spark Plasma Sintering
Transparent polycrystalline spinel ceramic was fabricated without any sintering aids by spark plasma sintering method of a mixture of Al2O3 and MgO powders for only 10min soak at 1250°C. Densification, microstructure and optical transparency of spinel were examined. The spinel exhibits an in-line transmission of 55% for a visible-wavelength of 470nm and high hardness value of 2040 HV.
متن کامل