Kinetic modelling of phenols consumption during polyethylene thermal oxidation
نویسنده
چکیده
Irganox 1010 stabilized PE was monitored by carbonyl build-up and DSC under oxygen. A scheme for PE stabilization by phenols was implemented and its kinetic parameters were calculated from experimental results. This model was validated from its ability to simulate kinetics curves for carbonyl build up, induction period changes with stabilizer concentration, and stabilizer depletion curve in thermal ageing. The use of OIT measurement for quantifying stabilizer is also discussed. Kinetic analysis showed that OIT is actually proportional to stabilizer concentration in virgin samples but this is not true for aged samples because of negative influence of oxidation unstable by-products. The model was also employed for discussing some scenarii proposed as explanation of heterogeneity observed during thermal oxidation of stabilized polyolefins.
منابع مشابه
Co-oxidation kinetic model for the thermal oxidation of polyethylene-unsaturated substrate systems
The thermal oxidation of polyethylene (PE) impregnated by the methyl esters of unsaturated fatty acids (UFEs) was studied using chemiluminescence, and infra-red spectrophotometry. It was shown that the presence of UFEs accelerates the PE aging process. This can be interpreted as a co-oxidation phenomenon. In this study, the previously established models for PE and UFEs self-oxidation have been ...
متن کاملThermal and catalytic degradation study of polyethylene and investigation the catalytic effect of X-Zeolite and Silica-Alumina on degradation kinetic
The thermal degradation of polyethylene (PE) was carried out in the absence and presence ofcatalystes X-Zeolite and Silica-Alumina at different temperatures. The optimum PE/Catalysisratio was 0.25:0.05 g/g, which produced highest degradation value. PE and PE/Catalysis werecharacterized by thermogravimetric analysis. The thermal degradation properties of polymerhave been studied by Infrared spec...
متن کاملThermo-Oxidation and Biodegradation Study of Low-Density Polyethylene /Starch Films by IR Spectroscopy
This article reports a study of the thermo-oxidation and biodegradation in the soil of low-density polyethylene/starch films (LDPE/starch) by infrared spectroscopy: Films of LDPE/Starch blends of different composition (starch content range from 0 to 15% w/w),were prepared and exposed to thermo-oxidation at different temperatures at 80, 90 and 100°C,and buried in the soil of public dump duri...
متن کاملInfluence of Operational Parameters and Kinetic Modelling of Catalytic Wet Air Oxidation of Phenol by Al/Zr Pillared Clay Catalyst
Single and mixed oxide Al/Zr-pillared clay (Al/Zr-PILC) catalysts were synthesized and tested for catalytic wet air oxidation (CWAO) of aqueous phenol solution under milder conditions, in a semi-batch reactor. The catalysts were synthesized from natural bentonite clay using ultrasonic treatment during the aging and intercalation steps and were characterized <...
متن کاملEffects of cadmium on manganese peroxidase competitive inhibition of MnII oxidation and thermal stabilization of the enzyme.
Inhibition of manganese peroxidase by cadmium was studied under steady-state and transient-state kinetic conditions. CdII is a reversible competitive inhibitor of MnII in the steady state with Ki approximately 10 microM. CdII also inhibits enzyme-generated MnIII-chelate-mediated oxidation of 2,6-dimethoxyphenol with Ki approximately 4 microM. CdII does not inhibit direct oxidation of phenols su...
متن کامل