Crystal structure of thiogermanic acid H(4)Ge(4)S(10).

X-ray diffraction analysis reveals the thiogermanic acid H(4)Ge(4)S(10) possesses discrete adamantane-like Ge(4)S(10)(4)(-) complex anions. Each thioanion is composed of four corner shared GeS(2.5)(-) tetrahedral units. Crystals were grown from anhydrous liquid hydrogen sulfide reactions with glassy germanium sulfide at room temperature. The crystal structure was solved and refined from single crystal diffractometer data (Mo Kalpha radiation) obtained at 173 K. H(4)Ge(4)S(10) is triclinic, centrosymmetric space group Ponemacr;, with a = 8.621(4) A, b = 9.899(4) A, c = 10.009(4) A, alpha = 85.963(7) degrees, beta = 64.714(7) degrees, gamma = 89.501(8) degrees, and Z = 2. Average bridging and terminal d(Ge-S) distances are 2.229 and 2.206 A, respectively. Vibrational mode assignments are reported from Raman scattering and IR absorption spectra of polycrystalline samples. The nu(s)(Ge-S-Ge) and nu(s)(Ge-S(-)) stretching modes are observed at 354 and 405 cm(-)(1), respectively.