A Novel Approach to Estimate the Plastic Anisotropy of Metallic Materials Using Cross-Sectional Indentation Applied to Extruded Magnesium Alloy AZ31B
نویسندگان
چکیده
In this paper, a methodology is presented for obtaining the plastic anisotropy of bulk metallic materials using cross-sectional indentation. This method relies on spherical indentation on the free edge of a specimen, and examining the out-of-plane residual deformation contour persisting on the cross-section after unloading. Results obtained from numerical simulation revealed that some important aspects of the out-of-plane residual deformation field are only sensitive to the extent of the material plastic anisotropy, and insensitive to strain hardening, yield strain, elastic anisotropy, and the selected displacement threshold value. An explicit equation is presented to correlate the plastic anisotropy with the characteristic parameter of the bottom shape of residual deformation contour, and it is used to uniquely determine the material plastic anisotropy in cross-sectional indentation. Effectiveness of the proposed method is verified by application on magnesium alloy AZ31B, and the plastic anisotropy parameter obtained from indentation and uniaxial tests show good agreement.
منابع مشابه
Load Controlled Fatigue of AZ31B
With the expanding demand on application of magnesium alloys in automotive and aerospace industries, robust methods in fatigue characterization of commercially available magnesium alloys with high specific strength is anticipated. In this paper, rotating bending load controlled tests has been studied on specimens machined from an extrusion piece of AZ31B. Due to asymmetric and anisotropic behav...
متن کاملA new low cycle fatigue lifetime prediction model for magnesium alloy based on modified plastic strain energy approach
Nowadays, the technology intends to use materials such as magnesium alloys due to their high strength to weight ratio in engine components. As usual, engine cylinder heads and blocks has made of various types of cast irons and aluminum alloys. However, magnesium alloys has physical and mechanical properties near to aluminum alloys and reduce the weight up to 40 percents. In this article, a new ...
متن کاملGrain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy
The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new interme...
متن کاملPLASTIC DEFORMATION BEHAVIOUR AT THE WORN SURFACE OF NOVEL CAST AL-ALLOY-TICP COMPOSITE
An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (`3-^9) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction....
متن کاملMechanical Behavior of AZ31B Mg Alloy Sheets under Monotonic and Cyclic Loadings at Room and Moderately Elevated Temperatures
Large-strain monotonic and cyclic loading tests of AZ31B magnesium alloy sheets were performed with a newly developed testing system, at different temperatures, ranging from room temperature to 250 °C. Behaviors showing significant twinning during initial in-plane compression and untwinning in subsequent tension at and slightly above room temperature were recorded. Strong yielding asymmetry and...
متن کامل