Modulated Structures, Nanocrystals and Quasicrystals in Mg-Zn-Y Alloys
نویسنده
چکیده
The formation of the icosahedral phase, BCC (Body centred cubic) phase and nanocrystals are seen in the as-cast alloy with nominal composition of Mg4Zn94Y2. FCC (face centred cubic) phase and modulated structures are formed in the alloys with higher Y content (10% and 25% Y respectively). These phases are analysed keeping in view their relation to the quasicrystals of the Mg-Zn-Y system.
منابع مشابه
Direct observation of solid-state reversed transformation from crystals to quasicrystals in a Mg alloy
Phase transformation of quasicrystals is of interest in various fields of science and technology. Interestingly, we directly observed unexpected solid-state epitaxial nucleation and growth of Zn6Mg3Y icosahedral quasicrystals in a Mg alloy at about 573 K which is about 300 K below the melting point of Zn6Mg3Y, in contrast to formation of quasicrystals through solidification that was usually fou...
متن کاملOne-step synthesis of alloyed dual-emitting semiconductor nanocrystals.
Alloyed Zn(1-x-y)Cd(x)Mn(y)Se nanocrystals exhibiting bright intrinsic dual emission attractive for ratiometric optical nanothermometry are reported. Relative to earlier materials with related dual emission, these alloy nanocrystals require shorter syntheses, contain less Cd(2+), and show dual emission that is less sensitive to nanocrystal shape, size, or surfaces.
متن کاملQuasicrystal-reinforced Mg alloys
The formation of the icosahedral phase (I-phase) as a secondary solidification phase in Mg-Zn-Y and Mg-Zn-Al base systems provides useful advantages in designing high performance wrought magnesium alloys. The strengthening in two-phase composites (I-phase + α-Mg) can be explained by dispersion hardening due to the presence of I-phase particles and by the strong bonding property at the I-phase/m...
متن کاملQuasicrystal-reinforced Mg alloys
The formation of the icosahedral phase (I-phase) as a secondary solidification phase in Mg–Zn–Y and Mg–Zn–Al base systems provides useful advantages in designing high performance wrought magnesium alloys. The strengthening in two-phase composites (I-phase + α-Mg) can be explained by dispersion hardening due to the presence of I-phase particles and by the strong bonding property at the I-phase/m...
متن کاملBiodegradable Mg-Zn-Y alloys with long-period stacking ordered structure: optimization for mechanical properties.
To optimize the mechanical properties for biodegradable orthopedic implant, microstructures and tensile properties of Mg-Zn-Y alloys containing long period stacking ordered (LPSO) phase were investigated. For the as-cast Mg(100-3x)(Zn(1)Y(2))(x) (1 ≤ x ≤ 3) alloys, volume fraction of 18R LPSO phase increases with increasing the contents of Zn and Y. Mg(97)Zn(1)Y(2) alloy exhibits the optimal co...