A study of room-temperature LixMn1.5Ni0.5O4 solid solutions
نویسندگان
چکیده
Understanding the kinetic implication of solid-solution vs. biphasic reaction pathways is critical for the development of advanced intercalation electrode materials. Yet this has been a long-standing challenge in materials science due to the elusive metastable nature of solid solution phases. The present study reports the synthesis, isolation, and characterization of room-temperature LixMn1.5Ni0.5O4 solid solutions. In situ XRD studies performed on pristine and chemically-delithiated, micron-sized single crystals reveal the thermal behavior of LixMn1.5Ni0.5O4 (0 ≤ x ≤ 1) cathode material consisting of three cubic phases: LiMn1.5Ni0.5O4 (Phase I), Li0.5Mn1.5Ni0.5O4 (Phase II) and Mn1.5Ni0.5O4 (Phase III). A phase diagram capturing the structural changes as functions of both temperature and Li content was established. The work not only demonstrates the possibility of synthesizing alternative electrode materials that are metastable in nature, but also enables in-depth evaluation on the physical, electrochemical and kinetic properties of transient intermediate phases and their role in battery electrode performance.
منابع مشابه
Preparation of Nickel Nanoparticles by Intramolecular Reaction of Nickel(II) Hydrazine Complex in the Solid State at Room Temperature
Ni6(N2H4)6(SO4)4(OH)2(H2O)8](SO4)(H2O)10 complex was prepared according to literature report. The reaction between aforementioned complex via sodium alkoxides as a reactants, were carried out in the solid state. The [Ni6(N2H4)6(SO4)4(OH)2(H2O)8](SO4)(H2O)10 undergoes an intramolecular two electrons oxidation-reduction reaction at room temperature and metallic nickel nanoparticles (Ni1-Ni5) was ...
متن کاملThe study of humidity effect on carbon dioxide gas sensing properties of zinc oxide nanowires assisted by polyvinyl alcohol network at room temperature
In this research, Zinc oxide (ZnO) nanostructures were synthesized by low cost hydrothermal method. The grown ZnO nanostructures had a dispersed distribution with nanowire morphology and the specific surface area of about 7 m2.gr-1 which they have crystalized in hexagonal wurtzite structure. ZnO nanowires/polyvinyl alcohol network (ZP) on the epoxy glass substrate with cu-interdigited electrods...
متن کاملA Study of Na/K Feldspar Solid Solution Using Statistical Mechanics
Thermal behavior of various solid feldspars are different, namely those of bivalent cations show no change in the distribution of Al and Si atoms, whereas feldspars of univalent cations become more disordered with raising temperature. In the latter case Al atoms migrate from the sites they occupe at low temperatures and interchange positions with the Si atoms. At high temperatures (but stil...
متن کامل[B(OH)3]0.78[B(OH)2(OSO3H)]0.22 as a new, cheap and eco-friendly catalyst for synthesis of acylals at room temperature under solvent free conditions
[B(OH)3]0.78[B(OH)2(OSO3H)]0.22 or (BSA) was simply prepared by addition of chlorosulfonic acid to commercial boric acid at room temperature. This cheap and green solid acid was used as an efficient catalyst for synthesis of acylals from aldehydes under solvent-free conditions at room temperature.
متن کامل[B(OH)3]0.78[B(OH)2(OSO3H)]0.22 as a new, cheap and eco-friendly catalyst for synthesis of acylals at room temperature under solvent free conditions
[B(OH)3]0.78[B(OH)2(OSO3H)]0.22 or (BSA) was simply prepared by addition of chlorosulfonic acid to commercial boric acid at room temperature. This cheap and green solid acid was used as an efficient catalyst for synthesis of acylals from aldehydes under solvent-free conditions at room temperature.
متن کامل