Observation of perpendicular magnetic anisotropy in Ni/Pt multilayers at room temperature
نویسندگان
چکیده
We report the experimental observation of room-temperature perpendicular magnetic anisotropy in Ni/Pt multilayers having 7–26 Å Ni and 2.3–4.6 Å Pt layer thicknesses, prepared by dc magnetron sputtering on glass substrates at 7 mTorr Ar sputtering pressure. Perpendicular magnetic anisotropy was found to be sensitively dependent on both Niand Pt-layer thicknesses, and a maximum anisotropy energy of 1.74310 erg/cm was obtained for (16 Å Ni/2.3 Å Pt)30 multilayer. Interestingly, magnetization measurements revealed that about two atomic layers of Ni at the interface were magnetically dead in our samples. © 1998 American Institute of Physics. @S0003-6951~98!01829-4#
منابع مشابه
Origin of room-temperature perpendicular magnetic anisotropy in Ni/Pt multilayers
Room-temperature perpendicular magnetic anisotropy ~PMA! was observed in Ni/Pt multilayer films having 7–30 Å Ni and constant 3 Å Pt sublayer thickness, prepared by magnetron sputtering at an Ar sputtering pressure of 7 mTorr. To understand the origin of PMA, the magnetoelastic anisotropy was determined from delicate in situ stress and ex situ magnetostriction coefficient measurements. Tensile ...
متن کاملRoom-temperature perpendicular magnetic anisotropy in Ni/Pd „111... multilayers
We report the experimental observation of room-temperature perpendicular magnetic anisotropy ~PMA! in Ni/Pd ~111! multilayer films having the thickness range of 5–11 Å Ni and 4–11 Å Pd sublayers, prepared by direct current magnetron sputtering on glass substrates at Ar sputtering pressure of 7 mTorr. Perpendicular magnetic anisotropy was found to be sensitively dependent on both Niand Pd-sublay...
متن کاملMagnetic Properties and Structural Study of Ni-Co/Cu Multilayers Prepared by Electrodeposition Method
Ni-Co/Cu multilayers have been grown by electrodeposition method from a single electrolyte (based on Ni(SO4).6H2O, Co(SO4).7H2O, Cu(SO4) and H3BO3) using galvanostatic control on titanium sublayers. The X-ray diffraction (XRD) patterns confirmed the multilayered structure with the nanometer thicknesses. Also, electron diffraction x-ray (EDX) analysis confirmed the purity of deposited samples. ...
متن کاملEvolution of magnetic domain reversal with temperature in Co ÕPt multilayers observed by magneto-optical Kerr imaging
The evolution of magnetic domain structures with temperature during magnetic reversal in Co 4 Å /Pt tPt multilayers with perpendicular anisotropy has been investigated using magneto-optical Kerr imaging. Relatively large Pt layer thicknesses tPt=43 and 63 Å are chosen for this study because the interlayer coupling strength in the multilayers varies from weak at room temperature to strong at low...
متن کاملPerpendicular Magnetic Anisotropy in Ion Beam
Co/Ni multilayers display perpendicular magnetic anisotropy and have applications in magnetic devices that could lead to a large increase in the density of magnetic storage. Co/Ni 10-(2 A Co/ 8A Ni) and 10-(2 A Co/ 4A Ni) multilayers were deposited with ion beam sputtering on either ion beam sputtered copper or direct current magnetron sputtered gold buffer layers of various thicknesses. The ef...