Effects of 2,2,2-trifluoroethyl methacrylate on properties of autopolymerized hard direct denture reline resins.

نویسندگان

  • Kazuhiro Yoshida
  • Tadafumi Kurogi
  • Tetsurou Torisu
  • Ikuya Watanabe
  • Hiroshi Murata
چکیده

This study evaluated the effects of the fluorinated monomer of 2,2,2-trifluoroethyl methacrylate (TFEMA) on the properties of autopolymerized hard direct denture reline resins. Iso-butyl methacrylate (i-BMA) and 2-hydroxyethyl methacrylate (2-HEMA) containing 30% TFEMA by weight were used as monomers, while poly(ethyl methacrylate) was used as a powder. Setting characteristics, dynamic mechanical properties, and changes over time, as well as wettability were determined by use of an oscillating rheometer, dynamic viscoelastometer, and contact angle meter. Water absorption and solubility were also measured according to ISO specifications. The reline resin based on i-BMA had greater elasticity and stiffness properties, while that based on 2-HEMA showed fewer dynamic mechanical property changes over time with the addition of TFEMA. Furthermore, water absorption and solubility tended to be reduced and contact angle increased. The results of this study suggest that TFEMA improves mechanical properties and durability of reline resins over time.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Influence of composition and powder/liquid ratio on setting characteristics and mechanical properties of autopolymerized hard direct denture reline resins

Reline of ill-fitting complete and removable partial dentures enhances their stability and retention by improving the adaptation between the denture intaglio surface and denture-bearing mucosa1). In clinical situations, that reline procedure is usually performed using a direct (chair-side reline system) rather than indirect (laboratory-processed reline system) method, because the former is more...

متن کامل

Dynamic mechanical properties of hard, direct denture reline resins.

STATEMENT OF PROBLEM Dynamic mechanical properties of hard, direct reline resins are important factors in the clinical success of dentures. However, little information is available on the nature of these properties. PURPOSE This study evaluated the dynamic mechanical properties of a variety of hard, direct reline resins: (1) visible light-polymerized, powder-liquid type, (2) visible light-pol...

متن کامل

Evaluation of glass transition temperature and dynamic mechanical properties of autopolymerized hard direct denture reline resins.

This study assessed methods for evaluation of glass transition temperature (Tg) of autopolymerized hard direct denture reline resins using dynamic mechanical analysis and differential scanning calorimetry in addition to the dynamic mechanical properties. The Tg values of 3 different reline resins were determined using a dynamic viscoelastometer and differential scanning calorimeter, and rheolog...

متن کامل

Influence of thickness increase of intraoral autopolymerizing hard denture base liners on the temperature rise during the polymerization process.

STATEMENT OF PROBLEM Increasing the thickness of intraoral autopolymerizing hard denture base liners may result in a temperature rise and a burning sensation for patients. PURPOSE The purpose of the study was to determine whether increasing the thickness of hard autopolymerizing reline resin increases the temperature of the basal seat area of a denture during the polymerization process. MAT...

متن کامل

A comparative evaluation of impact strength of conventionally heat cured and high impact heat cured polymethyl methacrylate denture base resins: an in vitro study.

UNLABELLED The denture bases made by using polymethyl methacrylates of Acrylic resin family have excellent physical properties, simple to process and easy to reline, rebase and repair. One of the inherent disadvantages of this material is the liability to break during function. The strength assessment of acrylic resins have been made generally by transverse defection tests. AIM To evaluate th...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:
  • Dental materials journal

دوره 32 5  شماره 

صفحات  -

تاریخ انتشار 2013