Infrared broadband emission of bismuth-doped barium-aluminum-borate glasses.

نویسندگان

  • Xian-Geng Meng
  • Jian-Rong Qiu
  • Ming-Ying Peng
  • Dan-Ping Chen
  • Quan-Zhong Zhao
  • Xiong-Wei Jiang
  • Cong-Shan Zhu
چکیده

We report near infrared broadband emission of bismuth-doped barium-aluminum-borate glasses. The broadband emission covers 1.3microm window in optical telecommunication systems. And it possesses wide full width at half maximum (FWHM) of ~200nm and long lifetime as long as 350micros. The luminescent properties are quite sensitive to glass compositions and excitation wavelengths. Based on energy matching conditions, we suggest that the infrared emission may be ascribed to 3P1? 3P0 transition of Bi+. The broad infrared emission characteristics of this material indicate that it might be a promising candidate for broadband optical fiber amplifiers and tunable lasers.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Near infrared broadband emission of bismuth-doped aluminophosphate glass.

Near infrared broadband emission characteristics of bismuth-doped aluminophosphate glass have been investigated. Broad infrared emissions peaking at 1210nm, 1173nm and 1300nm were observed when the glass was pumped by 405nm laser diode (LD), 514nm Ar+ laser and 808nm LD, respectively. The full widths at half maximum (FWHMs) are 235nm, 207nm and 300nm for the emissions at 1210nm, 1173nm and 1300...

متن کامل

Structural Investigation, Physical and Optical Properties of Mixed Alkali Bismuth Borate Glasses

Lead free, eco-friendly bismuth borate glasses doped with alkali oxides of composition xLi2O+(30-x)Na2O+55B2O3+15Bi2O3 (x = 5,10,15,20,25) were prepared by melt quenching technique. Amorphous nature of glasses was confirmed by X-ray diffraction. Density measurements were carried out at room temperature by standard principle of Archimedes with Xylene as an immersion liquid. The non-linear ...

متن کامل

Ce3+/Yb3+/Er3+ triply doped bismuth borosilicate glass: a potential fiber material for broadband near-infrared fiber amplifiers

Erbium doped bismuth borosilicate (BBS) glasses, possessing the broadest 1.55 μm near infrared (NIR) emission band among oxide glasses, stand out as excellent fiber material for optical fiber amplifiers. In this work, we demonstrate that both broadened and enhanced NIR emission of Er(3+) can be obtained by sensibly combining the effects such as mixed glass former effect, phonon-assisted energy ...

متن کامل

Doped Zinc Lithium Bismuth Borate Glasses

Zinc lithium bismuth borate glasses containing Er in (25x): Bi2O3:20Li2O:20ZnO: 35B2O3:xEr2O3 (where x=1, 1.5,2 mol %) have been prepared by melt-quenching method. The amorphous nature of the glasses was confirmed by x-ray diffraction studies. Optical absorption and fluorescence spectra were recorded at room temperature for all glass samples. Judd-Ofelt intensity parameters Ωλ (λ=2, 4, 6) are e...

متن کامل

Microwave Absorption of Barium Borosilicate, Zinc Borate, Fe-Doped Alumino-Phosphate Glasses and Its Raw Materials

This study presents microwave absorption of raw materials used in barium borosilicate, Fe-doped alumina phosphate and zinc borate glass. Microwave absorption was investigated for the raw materials SiO2, Na2CO3, BaCO3, BPO4, Al(PO3)3, Mg(PO3)2, Al(OH)3, TiO2. The study shows that SiO2 could be heated directly above 1000 °C within 30 min at 1.5 kW microwave output (MW) power and 0.8 kW MW power i...

متن کامل

ذخیره در منابع من

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Optics express

دوره 13 5  شماره 

صفحات  -

تاریخ انتشار 2005