Electron Conditioning of Technical Aluminium Surfaces: Effect on the Secondary Electron Yield
نویسنده
چکیده
The effect of electron conditioning on commercially aluminium alloys 1100 and 6063 were investigated. Contrary to the assumption that electron conditioning, if performed long enough, can reduce and stabilize the SEY to low values (≤ 1.3, value of many pure elements [1]), the SEY of aluminium did not go lower than 1.8. In fact, it reincreases with continued electron exposure dose.
منابع مشابه
EUROPEAN ORGANIZATION FOR NUCLEAR RESEARCH CERN - ACCELERATORS AND TECHNOLOGY SECTOR Secondary Electron Yield on Cryogenic Surfaces as a Function of Physisorbed Gases
Electron cloud is a serious limitation for the operation of particle accelerators with intense positively charged beams. It occurs if the secondary electron yield (SEY) of the beam-pipe surface is sufficiently high to induce an electron multiplication. At low surface temperatures, the SEY is strongly influenced by the nature of the physisorbed gases and by the corresponding surface coverage. Th...
متن کاملElectron Conditioning of Technical Aluminium Surfaces
This note do consider a conventional conversion target and th Since the length of the i concurrent pressure puls of T
متن کاملSummary of SLAC’S SEY Measurement On Flat Accelerator Wall Materials
The electron cloud effect (ECE) causes beam instabilities in accelerator structures with intense positively charged bunched beams. Reduction of the secondary electron yield (SEY) of the beam pipe inner wall is effective in controlling cloud formation. We summarize SEY results obtained from flat TiN, TiZrV and Al surfaces carried out in a laboratory environment. SEY was measured after thermal co...
متن کاملEFFECT OF HEAT INPUT ON THE STRUCTURE AND PROPERTIES OF ALUMINIUM WELDMENT
The probable reasons for evolution of weld porosity and solidification cracking and the structure- property relationship in aluminium welds were investigated. Aluminium plates (1xxx series) were welded by Tungsten Inert Gas (TIG) welding process, 5356 filler metal was used and heat input was controlled by varying welding current (145A, 175A and 195A). The welded samples were examined under opti...
متن کاملElectron Cloud in the Sps Summary
• The first talk by F. Ruggiero [1] gave a short introduction to some key concepts relevant to the discussion of electron cloud effects and their implications for PS, SPS and LHC operation. • This was followed by a talk given by W. Höfle [2] who reported about strong perturbations on pick-up signals of the SPS transverse feedback system (damper), observed with LHC type beams and attributed to t...
متن کامل