Effects of photo-assisted electrodeposited on CuInSe2 thin films
نویسندگان
چکیده
Photo-assisted one-step electrodeposition has been applied to help in forming smooth and dense CuInSe2 films. The difference in surface morphology and crystalline quality between CuInSe2 films with various photo-assistance has been investigated. In the photo-assisted electrodeposition process, the many kinds of lamps providing maximum light intensity at about 380 to 620 nm were used as light source to be irradiated onto the surface of Mo-coated soda-lime glass substrates. The results suggested effects of photo-assistance including activating surface diffusion and growing high-crystalline quality films with reduced defects during electrodeposition.
منابع مشابه
ONE STEP ELECTRODEPOSITION OF CuInSe2 THIN FILMS
Formation of CuInSe2 (CIS) thin films from aqueous solution containing citrate as complexing agent is reported. The surface morphology and the composition of the deposited films are characterized by scanning electron microscopy (SEM). The texture of the deposits and their compositions are analyzed by X-ray diffraction and transmission electron microscopy (TEM). Annealing of the films at 350°C i...
متن کاملSurfactant-Assisted Electrodeposition of CoFe-Barium Hexaferrite Nanocomposite Thin Films
The influences of anionic sodium dodecylsulfate (SDS) and cationic Hexadecyltrimethylammonium bromide (HTAB) surfactants on the incorporation and distribution of barium hexaferrite nanoparticles in the electrodeposited CoFe-BaFe12O19 composite thin films were studied. Sulphate bathes with natural pH containing 0 to 2 g/L surfactants were used for electroplating at room temperature. Field emissi...
متن کاملFabrication of Nb/V co-doped TiO2 thin films and study of structural, optical and photocatalytic properties
In this study, different samples of Niobium and Vanadium co-doped titania thin films (5-10-15 mol% Nb and 5-10-15 mol% V) were prepared via sol−gel dip coating method, using niobium chloride as niobium precursor, ammonium metavanadate as vanadium precursor, and titanium (IV) butoxide (TBT) as titanium precursor. The effects of doping amount on the structural, optical, and photo-catalytic prope...
متن کاملFabrication of Nb/V co-doped TiO2 thin films and study of structural, optical and photocatalytic properties
In this study, different samples of Niobium and Vanadium co-doped titania thin films (5-10-15 mol% Nb and 5-10-15 mol% V) were prepared via sol−gel dip coating method, using niobium chloride as niobium precursor, ammonium metavanadate as vanadium precursor, and titanium (IV) butoxide (TBT) as titanium precursor. The effects of doping amount on the structural, optical, and photo-catalytic prope...
متن کاملSynthesis of CuInSe2 thin films from electrodeposited Cu11In9 precursors by two-step annealing
In this study, copper indium selenide (CIS) films were synthesized from electrodeposited Cu-In-Se precursors by two-step annealing. The agglomeration phenomenon of the electrodeposited In layer usually occurred on the Cu surface. A thermal process was adopted to turn Cu-In precursors into uniform Cu11In9 binary compounds. After deposition of the Se layer, annealing was employed to form chalcopy...
متن کامل