Fatigue Damage Evolution in Silicon Films for Micromechanical Applications
نویسندگان
چکیده
In this paper we examine the conditions for surface topography evolution and crack growth/fracture during the cyclic actuation of polysilicon microelectromechanical systems (MEMS) structures. The surface topography evolution that occurs during cyclic fatigue is shown to be stressassisted and may be predicted by linear perturbation analyses. The conditions for crack growth (due to pre-existing or nucleated cracks) are also examined within the framework of linear elastic fracture mechanics. Within this framework, we consider pre-existing cracks in the topical SiO2 layer that forms on the Si substrate in the absence of passivation. The thickening of the SiO2 that is normally observed during cyclic actuation of Si MEMS structures is shown to increase the possibility of stable crack growth by stress corrosion cracking prior to the onset of unstable crack growth in the SiO2 and Si layers. Finally, the implications of the results are discussed for the prediction of fatigue damage in silicon MEMS structures. KEY WORDS-Fatigue, polysilicon, MEMS, surface topography evolution, crack growth
منابع مشابه
Fatigue behavior and damage modeling of SCS-6/titanium/titanium aluminide hybrid laminated composite
The fatigue behavior of the unnotched and notched silicon carbide fiber-reinforced titanium/titanium aluminide hybrid laminated composite was investigated at room temperature. The evolution of microstructural damage and its effect on stiffness and strength degradation was quantified as a function of loading cycles and applied stress levels. Fatigue crack propagation behavior and damage mechanis...
متن کاملHigh-cycle Fatigue in Micron-scale Structural Films of Polycrystalline Silicon: a Reaction-layer Failure Mechanism
A study has been made of high-cycle fatigue in 2-μm thick structural films of ntype, polycrystalline silicon for MEMS applications. Using an “on-chip” test structure resonating at ~40 kHz, such thin-film polysilicon is shown to display “metal-like” stress-life fatigue behavior in room air environments, with failures occurring after lives in excess of 10 cycles at stresses as low as half the fra...
متن کاملHigh-Cycle Fatigue of Polycrystalline Silicon Thin Films in Laboratory Air
When subjected to alternating stresses, most materials degrade, e.g., suffer premature failure, due to a phenomenon known as fatigue. It is generally accepted that in brittle materials, such as ceramics, cyclic fatigue can only take place where there is some degree of toughening, implying that premature fatigue failure would not be expected in polycrystalline silicon where such toughening is ab...
متن کاملEvaluation of continuum damage at different temperatures for aluminum-silicon alloy of engine piston within low-cycle fatigue regime
In this article, the isothermal low-cycle fatigue continuum damage in the engine piston aluminum alloy has been evaluated at different temperatures. For this objective, experimental data of low-cycle fatigue tests on standard specimens were used at 280, 350 and 425°C. Based on the continuum damage mechanics method, the fatigue damage was calculated during cyclic loading. Obtained results, inclu...
متن کاملFatigue of polycrystalline silicon for microelectromechanical system applications: crack growth and stability under resonant loading conditions
Although bulk silicon is not known to exhibit susceptibility to cyclic fatigue, micron-scale structures made from silicon films are known to be vulnerable to degradation by fatigue in ambient air environments, a phenomenon that has been recently modeled in terms of a mechanism of sequential oxidation and stress-corrosion cracking of the native oxide layer. To date, most stress-life (S=N ) fatig...
متن کامل