Increasing of Machine Parts Wear Resistance by Nanostruсturing
نویسنده
چکیده
This paper presents the scientific rationale for the use of a new generation of functionally graded nano-(L = 50-500 nm) based on the Al-N, Ti-N, Ti-C, Al-O and Mo-S nanolayers (l = 1-10nm) on steel to improve durability for operation in extreme operating conditions of parts and units of machines and mechanisms
منابع مشابه
Comparison of Carburizing and Boronizing Processes on Mechanical and Wear Properties of PM Parts
In this study carburizing and boronizing processes were applied to powder metallurgy steel specimens and the mechanical and tribological properties of the substrate and coatings were evaluated under various process conditions. The specimens, made from industrial test pieces, were carburized in a powder pack for a duration of 2-5 hrs at 850-950 ˚C. Similar specimens were pack boronized for 4 hr...
متن کاملImproving the surface wear resistance of aluminum by electrical discharge process
In this study electrical discharge process was used to increase surface wear resistance of pure aluminum. Pulse-on-time and pulse current were considered as input parameters of the electrical discharge process. Experimental results reveal that the electrical discharge process is a successful method for improving the surface wear resistance of aluminum, so that this method has greatly increased ...
متن کاملبررسی اثر نوع فیلر بر سایش سه جزئی کامپوزیت دندانی
Statement of Problem: The relatively poor wear resistance of dental composite in stress bearing posterior situations has restricted wider clinical application of this restorative material. Purpose: The aim of this study was to evaluate the three body abrasive wear of a dental composite based on a new filler (leucite: KAl Si2O6) and to compare it with the wear resistance of a composite based on ...
متن کاملComparison of Carburizing and Boronizing Processes on Mechanical and Wear Properties of PM Parts
In this study carburizing and boronizing processes were applied to powder metallurgy steel specimens and the mechanical and tribological properties of the substrate and coatings were evaluated under various process conditions.
The specimens, made from industrial test pieces, were carburized in a powder pack for a duration of 2-5 hrs at 850-950 ˚C. Similar specimens were pack boronized for 4 ...
متن کاملA New Method of Surface Hardening of Steel by Borozar-p Boronizing Paste
The BOROZAR-P boronizing paste is used for thermo chemical treatment of steel machine tools and parts for enhancing their wear-resistance, i.e. extending their useful life-time. Boronizing in this case leads to hardening of the thermally treated surfaces. This new method comprises the formation of wearand corrosionresistant surface layer with minimum loss of time and expenses. The thus obtained...