Biasing Voltage Dependence of Sensitivity of Electron Beam Evaporated SnO2 Thin Film CO Sensor
نویسندگان
چکیده
Thin films of tin oxide were deposited by electron beam evaporation. The effects of the sensor biasing voltage and film thickness on the CO-sensing of tin oxide thin films were investigated. The films were characterized using X-ray diffraction and X-ray photoelectron spectroscopy All the films were found to be amorphous. The current-voltage characteristic of the sensor in air has shown that semiconductor-metal interface forms Schottky barrier. It was found that the CO-sensing properties depend on the sensor biasing voltage and film thickness. For lower biasing voltages the sensitivity was much higher than for the higher voltages. It was found that the sensitivity of the films to CO increased with the film thickness.
منابع مشابه
Investigation of Physical Properties of e-Beam Evaporated CdTe Thin Films for Photovoltaic Application
CdTe thin films with 2.8 µm thickness were deposited by electron beam evaporation method. X-ray diffraction, scanning electron microscopy, UV-Vis-NIR spectroscopy and atomic force microscopy (AFM) were used to characterize the films. The results of AFM analysis revealed that the CdTe films have uniform surface. CdTe thin films were heat-treated by SnCl2 solution. Structural analysis using XRD s...
متن کاملThickness Dependence of Sensitivity in Thin Film Tin Oxide Gas Sensors Deposited by Vapor Pyrolysis
Transparent SnO2 thin films were deposited on porcelain substrates using a chemical vapor deposition technique based on the hydrolysis of SnCl4 at elevated temperatures. A reduced pressure self-contained evaporation chamber was designed for the process where the pyrolysis of SnCl4 at the presence of water vapor was carried out. Resistive gas sensors were fabricated by providing ohmic contacts o...
متن کاملTheoretical Investigation First Principles Study of Hydrogen Storage in SWCNT Functionalized with metal complexes (MgH2, TiO2 & SnO2)
The results of hydrogenation of single walled carbon nanotubes (SWCNTs)-SnO2 composite thin film is reported here. SWCNTs mixed with SnO2 by weight are made into pellet without any binder. Then, the pellet is evaporated by electron beam on glass substrates at room temperature in hydrogen atmosphere. The amount of hydrogen incorporated in the SWCNTs-SnO2 composite is found to be 2.4 wt.%. In add...
متن کاملBand-Gap Tuning Of Electron Beam Evaporated Cds Thin Films
The effect of evaporation rate on structural, morphological and optical properties of electron beam evaporated CdS thin films have been investigated. CdS thin film deposited by electron beam evaporation method in 12nm/min and 60nm/min evaporation rates on glass substrates. X-ray diffraction, scanning electron microscopy, UV-Vis-NIR spectroscopy and Atomic Force Microscopy were used to character...
متن کاملCharacterization of nanostructured SnO2 thin film coated by Ag nanoparticles
Nanostructured SnO2 thin films were prepared using Electron Beam-Physical Vapor Deposition (EB-PVD) technique. Then Ag nanoparticles synthesized by laser-pulsed ablation were sprayed on the films. In order to form a homogenous coated of SnO2 on the glass surface, it was thermally treated at 500°C for 1 h. At this stage, the combined layer on the substrate was completely dried for 8 h in the air...
متن کامل