Effect of Alloying Element of S, Se or Te on Oxidation Resistance of Cu at 573-873 K
نویسندگان
چکیده
The influence of alloying element S, Se or Te on the oxidation resistance of pure Cu was studied by oxidizing in 0.1 MPa pure oxygen atmosphere at 573-873 K in comparison with a 6N Cu (99.9999 wt.%). The addition of S, Se or Te is found to improve the oxidation resistance of Cu remarkably. This improvement is contributed from the accumulation of alloying element at the Cu2O/Cu interface and segregation of alloying elements at grain boundaries in Cu2O.
منابع مشابه
Investigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in 1, 3, and 6 of weight percentage compounds. The vial speed was 350 rpm and ball to powder weight ratio kept at 15:1 under Argon atmosphere, and the time of milling was 90 h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)....
متن کاملShape Memory Properties in Cu-Zn-Al Alloy
In this research a Cu-Zn-Al alloy is produced by melting the raw materials in an electric resistance furnace and then pouring it into a steel mould. The optimum way to achieve the final analysis in the hypo-eutectoid range is determined and the influence of the alloying element, Ti on the grain size and the shape memory properties of the samples are investigated. Solution treatment (done at 850...
متن کاملShape Memory Properties in Cu-Zn-Al Alloy
In this research a Cu-Zn-Al alloy is produced by melting the raw materials in an electric resistance furnace and then pouring it into a steel mould. The optimum way to achieve the final analysis in the hypo-eutectoid range is determined and the influence of the alloying element, Ti on the grain size and the shape memory properties of the samples are investigated. Solution treatment (done at 850...
متن کاملبررسی تأثیر ریزساختار بر مقاومت به اکسیداسیون آلیاژ Ti47Al48Mn5 تولید شده به روش آلیاژسازی مکانیکی
The aim of this investigation was to produce Ti47Al48Mn5 intermetallic compounds with different microstructures in order to study their oxidation behavior. The reason for selecting manganese as an alloying element was to enhance the toughness of the compound. Ti47Al48Mn5 alloys were obtained through mechanical alloying, cold pressing and heat treatment. XRD results showed that milling of the el...
متن کاملEffect of Ni on Amorphization of Ti-Cu-Ni Ternary alloys Prepared by Mechanical alloying
Amorphous alloys has been taken into consideration because of their unique properties and are nominated as the future engineering materials. In this research, the effect of Ni and milling time on amorphization process and thermal stability of Ti50Cu50-xNix(x=10, 15, 25 at%) alloy system were investigated. The evolution of amorphization during milling, thermal stability and subsequent heat treat...
متن کامل