Electrical conductivity measurements are reported for normal and deuterated ammonium chloride single crystals in the temperature regions which characterize the pure and the impurity-dominated materials. We conclude from the data that conductivity in ammonium chloride is due to the formation of either cation or anion vacancies and a subsequent process controlled by a proton transfer. Our results are found to be consistent with a model proposed by Herrington and Staveley.
منابع مشابه
Hopping Conductivity in Single Crystals (Cd0.6Zn0.32Mn0.08)3As2 (RESEARCH NOTE)
The growth processes of Tetragonal single crystals of solid solution (Cd0.6Zn0.32Mn0.08)3As2, space group P42/nmc, has been synthesized by Bridgman method. Conductivity and magnetoresistance of (Cd0.6Zn0.32Mn0.08)3As2 were measured in the range 1.6K to 300K and in magnetic field up to 25 T. Crossover from Mott variable-range-hopping conductivity mechanism close to helium temperatures. In this w...
متن کاملرشد تکبلور نیمرسانای Te04/0Zn96/0Cd به دو روش بریجمن تغییریافته و ترابری فاز بخار
Single crystals of Cd.96Zn.04Te (CZT) with 14 mm in diameter were grown by seedless modified Bridgman method. Also, crystals with the same chemical composition were grown by vapor phase inert gas-transport method (VPGT), and single crystals up to 3.5 mm in diameter were obtained. Structural studies by XRD and back reflection Laue method show that the grown crystals are single phase with high pu...
متن کاملرشد تکبلورهای Cd0.96Zn0.04Te به روش ترابری فاز بخار
Cd0.96Zn0.04Te crystals were grown using vapor phase gas transport method (VPGT). The results show that dendritic crystals with grain size up to 3.5 mm can be grown with this technique. X-ray diffraction and Laue back-reflection patterns show that dendritic crystals are single-phase, whose single crystal grains are randomly oriented with respect to the gas-transport axis. Electrical measureme...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملNew low-dimensional molecular metals: single-crystal electrical conductivity of nickel phthalocyanine iodide.
Single crystals of NiPcI(1.0) (Pc = phthalocyanine), which are composed of one-dimensional stacks of (NiPc)(+0.33) molecules and chains of I(3)(-) molecules, exhibit metallic electrical conductivity in the stacking direction. At room temperature the mean free path of the carrier is 3.3 to 8.2 angstroms.
متن کامل