Characterization of Nanocomposite Laminates Fabricated from Aqueous Dispersion of Nanoclay

Preparation of E-glass/waterborne epoxy prepregs containing natural nanoclay and properties of their composites are presented. Prepregs were prepared by wetting randomly oriented, chopped glass fiber preforms with aqueous dispersion of EpiRez 3522-W-60 resin, dicyandiamide, 2-methylimidazole and natural nanoclay (Cloisite Naþ). The nanoclay content of the aqueous dispersion was adjusted to yield final nanoclay contents of 0, 1, 2, and 4 wt%, whereas the glass fiber content is kept constant at 47 wt%. These prepregs were then used to fabricate disk-shaped composite samples by APA2000 rheometer. Composite samples were tested for interlaminar shear strength, flexural stiffness, and glass transition temperature. The flexural stiffness was observed to increase by more than 26% over the range of nanoclay loading, despite a 13% decrease in interlaminar shear strength. Similarly, glass transition temperature increased from 898C to above 948C for the samples comprising 4 wt% nanoclay. X-ray diffraction analyses indicated 48% increase in the gallery spacing suggesting strong intercalation of the nanoclay platelets by the epoxy matrix. Microstructural observations of the fracture surfaces and polished surfaces show significant differences in the matrix topology and fiber to matrix adhesion. The composites with higher nanoclay content depict uniform and submicron surface features implying homogenous dispersion of nanoclay. POLYM. COMPOS., 31:620–629, 2010. a 2009 Society of Plastics Engineers