Fe(3+) ions in alkali lead tetraborate glasses--an electron paramagnetic resonance and optical study.

Glass systems of composition 90R(2)B(4)O(7)+9PbO+1Fe(2)O(3) (R=Li, Na and K) and 90Li(2)B(4)O(7)+(10-x)PbO+xFe(2)O(3) (x=0.5, 1, 3, 4, 5, 7 and 9 mol %) have been investigated by means of electron paramagnetic resonance (EPR) and optical absorption techniques. The EPR spectra exhibit three resonance signals at g approximately 6.0, 4.2 and 2.0. The resonances at g approximately 6.0 and 4.2 are attributed to Fe(3+) ions in rhombic and axial symmetry sites, respectively. The g approximately 2.0 resonance signal is due to two or more Fe(3+) ions coupled together with dipolar interaction. The EPR spectra of 1 mol % of Fe(2)O(3) doped in lithium lead tetraborate glass samples have been studied at different temperatures (123-433 K). The intensity of g approximately 4.2 resonance signal decreases and the intensity of g approximately 2.0 resonance signal increases with the increase of temperature. The line widths are found to be independent of temperature. The EPR spectra exhibit a marked concentration dependence on iron content. A decrease in intensity for the resonance signal at g approximately 4.2 with increase in iron content for more than 4 mol % has been observed in lithium lead tetraborate glass samples and this has been attributed to the formation of Fe(3+) ion clusters in the glass samples. The paramagnetic susceptibility (chi) is calculated from the EPR data at various temperatures and the Curie constant (C) has been evaluated from 1/chi versus T graph. The optical absorption spectrum of Fe(3+) ions in lithium lead tetraborate glasses exhibits three bands characteristic of Fe(3+) ions in an octahedral symmetry. The crystal field parameter D(q) and the Racah interelectronic repulsion parameters B and C have also been evaluated. The value of interelectronic repulsion parameter B (825 cm(-1)) obtained in the present work suggests that the bonding is moderately covalent.