Rapid thermal annealing effects on the structural properties and density of defects in SiO2 and SiNx :H films deposited by electron cyclotron resonance
نویسندگان
چکیده
منابع مشابه
STUDY OF ANNEALING TEMPERATURE VARIATION ON THE STRUCTURAL PROPERTIES OF DIP-COATED TiO2-SiO2 NANOSTRUCTURED FILMS
Abstract:In the present research, SiO2–TiO2 nanostructure films were successfully prepared on windshields using the sol–gel technique for photocatalytic applications. To prevent the thermal diffusion of the sodium ions from the glass to TiO2 films, the SiO2 layer was pre-coated on the glass by the sol–gel method. The substrates were dipped in the sol and withdrawn with the speed of 6cm/min-1 to...
متن کاملEffects of Annealing and Thickness on the Structural and Optical Properties of Crystalline ZnS Thin Films Prepared by PVD Method
Zinc Sulfide (ZnS) thin films were deposited on glass substrates at the pressure of 10-6 mbar by thermal resistor evaporation technique. The effects of annealing on the structural, optical properties of ZnS films were studied. Crystalline ZnS films have been analyzed by X-ray diffraction. Only cubic phase with the preferred (111) plane was found in ZnS films. Optical characteristics were studie...
متن کاملInvestigation of Structural, Morphological and Optical Properties of Chromium Oxide Thin Films Prepared at Different Annealing Times
Chromium oxide (α-Cr2O3) thin films were prepared using thermal annealing of chromium (Cr)films deposited on quartz substrates by direct current (DC) magnetron sputtering. The annealingprocess of the films was performed for different times of 60, 120,180 and 240 min. The influenceof annealing time on structural, morphological and optical properties of the prepared films wasinvestigated by diffe...
متن کاملFormation of Cupric Oxide Films on Quartz Substrates by Annealing the Copper Films
In the present work, cupric oxide (CuO) films were obtained through thermal annealing of the copper (Cu) films deposited on quartz substrates by DC magnetron sputtering method. The annealing was performed in air atmosphere for different times ranging from 60-240 min at temperature of 400 ºC. The influence of annealing times on structural and morphological properties of the films was investi...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...