The Strain Hardening Behaviour of Supersaturated Al-Cu Alloys
نویسندگان
چکیده
Julien da Costa Teixeira, Yves Bréchet , Yuri Estrin and Christopher Hutchinson ARC Centre of Excellence for Design in Light Metals, Department of Materials Engineering, Monash University, Clayton, VIC, 3800, Australia Institut Jean Lamour, Dépt SI2M, Ecole des Mines, Parc de Saurupt, 54042 Nancy, France SIMAP, Institut Nationale Polytechnique de Grenoble, St. Matin D’Hères, 38000, France CSIRO Process Science and Engineering, Clayton South, 3168, VIC, Australia
منابع مشابه
Precipitates and intermetallic phases in precipitation hardening Al–Cu–Mg–(Li) based alloys
The present study contains a critical review of work on the formation of precipitates and intermetallic phases in dilute precipitation hardening Al–Cu–Mg based alloys with and without Li additions. Although many suggestions for the existence of pre-precipitates in Al–Cu–Mg alloys with a Cu/Mg atomic ratio close to 1 have been made, a critical review reveals that evidence exists for only two tru...
متن کاملSOLUTION STRENGTHENING AND AGE HARDENING CAPABILITY OF Al-Mg-Mn ALLOYS WITH SMALL ADDITIONS OF Cu
Nine Al-(1-3)Mg-(0-0.4)Cu-0.15Si-0.25Mn (in wt%) alloys with potential applications in both packaging and automotive industries have been investigated. Tensile testing showed that solution strengthening is in good approximation linearly proportional to the Mg content. Mechanical testing and microstructural examinations of aged samples indicate that Mg2Si phase precipitates contribute to age har...
متن کاملHigh-strength age hardening copper–titanium alloys: redivivus
In this review the decomposition of supersaturated Cu–Ti solid solutions and subsequent microstructural evolution are discussed in terms of modern views of precipitation from solid solution. This update is motivated by an anticipated emergence of these alloys as technologically significant high-strength, high-conductivity, precipitation hardened alloys over the next decade replacing conventiona...
متن کاملPLASTIC DEFORMATION BEHAVIOUR AT THE WORN SURFACE OF NOVEL CAST AL-ALLOY-TICP COMPOSITE
An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (`3-^9) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction....
متن کاملAge Hardening of Ultrafine Grained Al-Ti-Cr Alloys Fabricated by Continuous Electron Beam Evaporation
Supersaturated Al-Ti-Cr alloys were produced by a continuous electron beam evaporation technique. The as-deposited alloy sheets were fcc supersaturated solid solution with an average grain size of about 400 nm. Due to the fine grain size, the hardness of the alloy was as high as 270Hv. The sheet showed age hardening, and the peak hardness of 340Hv was obtained after aging at 623K for 900 s, in ...
متن کامل