Synthesis and characterization of diblock and gel-forming pentablock copolymers of tertiary amine methacrylates, poly(ethylene glycol), and poly(propylene glycol)
نویسندگان
چکیده
Novel pH-sensitive gel-forming pentablock copolymers based on commercially available Pluronic (poly(ethylene oxide)-b-poly(propylene oxide)-b-poly(ethylene oxide), PEO-b-PPO-b-PEO) triblock copolymers and cationic diblock copolymers based on polyethylene glycol) methyl ether (PEGME) were synthesized by oxyanionic polymerization. Polymerization of the cationic moiety, poly((diethylamino)-ethyl methacrylate), PDEAEM, was initiated by a difunctional potassium alcoholate of the triblock Pluronic copolymer F127 (PEO106-PPO69-PEO106) or PEGME. The difunctionality of the initiation using the triblock macroinitiator, indicating formation of a pentablock copolymer rather than a tetrablock copolymer, was verified by functionalized termination of the living polymer chains. Critical micellization temperatures (cmt) of the synthesized polymers were obtained from differential scanning calorimetry for the pentablock materials. The pentablock copolymers retained the thermoreversible gel-forming properties of Pluronic F127 as well as similar cmt values. The polydispersity of both the diblock and pentablock copolymers was similar to the macroinitiators, indicating a very low polydispersity associated with the addition of the cationic PDEAEM blocks. Both of the materials show pH-sensitive release behavior, whereas the native polymers do not.
منابع مشابه
Synthesis and Thermal Properties of Novel Biodegradable ABCBA Pentablock Copolymers from Poly (Ethylene glycol), L-Lactide and p-Dioxanone
In this work, new biodegradable ABCBA type pentablock copolymers with different mole ratio of L-lactide and PPDO-b-PEG-b-PPDO triblock copolymer were synthesized and characterized. In the first step, PPDO-b-PEG-b-PPDO triblock copolymer was synthesized via a ring-opening polymerization of P-DiOxanone (PDO) monomer with Poly (Ethylene Glycol) (P...
متن کاملStudy of Surface Tension of Binary Mixtures of Poly (Ethylene Glycol) in Water and Poly (Propylene Glycol) in Ethanol and its Modeling Using Neural Network
متن کامل
Docetaxel-Loaded Mixed Micelles and Polymersomes Composed of Poly (caprolactone)-Poly (ethylene glycol) (PEG-PCL) and Poly (lactic acid)-Poly (ethylene glycol) (PEG-PLA): Preparation and In-Vitro Characterization
Microwave irradiation was used to synthesize PEG-PCL and PEG-PLA copolymers that are composed of biodegradable polymers including PEG, PLA, and PCL. These copolymers were used for loading docetaxel in nanoparticles. Single emulsion-solvent evaporation technique was applied for preparing the PEG-PLA and PEG-PCL mixed nanoparticles (micelles and polymersomes) with different proportions, including...
متن کاملDocetaxel-Loaded Mixed Micelles and Polymersomes Composed of Poly (caprolactone)-Poly (ethylene glycol) (PEG-PCL) and Poly (lactic acid)-Poly (ethylene glycol) (PEG-PLA): Preparation and In-Vitro Characterization
Microwave irradiation was used to synthesize PEG-PCL and PEG-PLA copolymers that are composed of biodegradable polymers including PEG, PLA, and PCL. These copolymers were used for loading docetaxel in nanoparticles. Single emulsion-solvent evaporation technique was applied for preparing the PEG-PLA and PEG-PCL mixed nanoparticles (micelles and polymersomes) with different proportions, including...
متن کاملSynthesis of polysaccharide-b-PEG block copolymers by oxime click.
The oxime click reaction is shown to be a straightforward methodology for the synthesis of poly(ethylene glycol) (PEG)-polysaccharide diblock copolymers. The method is applicable to unmodified polysaccharides with a reductive end as demonstrated for dextran, hyaluronic acid and chitosan. Notably the oxime click reaction is applied for the first time to the end modification of polysaccharides.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2017