08490 - Water Effects on Adhesion and Wear Resistance of Chromium Oxide Coatings
نویسندگان
چکیده
Nano-scratch and nano-indentation were used to determine hardness, elastic modulus, adhesion, friction and wear resistance of chromium oxide coatings in air and in water. The friction coefficient is higher in water, compared to air, and it increases with the applied normal load, although there are no obvious differences in hardness and elastic modulus in air vs. water. A higher normal load increases the wear volume; while the wear rate decreases with the number of wear cycles due to machining hardening. A reduction in coating adhesion was observed in water when the normal load exceeded a critical value of 1.8 N.
منابع مشابه
Microstructure and mechanical properties of chromium oxide coatings
Chromium oxide coatings were deposited on low-carbon steel by radiofrequency reactive magnetron sputtering at different oxygen flux values. X-ray diffraction, x-ray photoelectron spectroscopy, and high-resolution transmission electron microscopy were used to investigate the microstructure of chromium oxide coatings. Varying oxygen flux changed the coating microstructure; as with increasing oxyg...
متن کاملPlasma spraying and characterization of chromium carbide – nickel chromium coatings
Chromium carbide – nickel chromium powder Cr3C2-25wt.NiCr was plasma sprayed by a water-stabilized system WSP®. A series of experiments with variable feeding distance was carried out. Basic characterization of coatings was done by XRD, SEM and light microscopy plus image analysis. Microhardness was measured on polished cross sections. The main focus of investigation was on resistances against w...
متن کاملInterfacial Microstructure of Chromium Oxide Coatings
Chromium oxide coatings are chemically inert, have high mechanical strength, hardness and good optical characteristics; therefore, they have been widely used in many applications including corrosion protection, wear resistance, electronics, and optics. Cr2O3 is well suited for wear resistance applications, as it is one of the hardest oxides with 29.5 GPa hardness. Several deposition techniques ...
متن کاملA New Method for Electroplating of Crack-Free Chromium Coatings
In this study, different amounts of MoS2 particles and an anionic surfactant were added to the conventional chromium electroplating bath in order to electrodeposite crack-free chromium coatings and the structure, morphology, tribology and corrosion behavior of the deposited coatings were investigated using X-ray diffraction spectroscopy, scanning electron microscopy, pin on disk ...
متن کاملStudy of multilayer and multi-component coatings deposited using cathodic Arc technique on H-13 hot work steel for die-casting applications
Die casting process is used since long, but even today problems like erosion, corrosion, soldering and sticking affect die life. These dies undergo thermal cyclic loads from 70 oC to 600 oC during processing. Physical Vapor Deposition (PVD) hard coating can play an important role in such extreme applications. In the present work, we report the use of Chromium based multila...