Microstructural aspects of fatigue in Ni-base superalloys.
نویسنده
چکیده
Nickel-base superalloys are primarily used as components in jet engines and land-based turbines. While compositionally complex, they are microstructurally simple, consisting of small (50-1000 nm diameter), ordered, coherent Ni(3)(Al,Ti)-type L1(2) or Ni(3)Nb-type DO(22) precipitates (called γ(') and γ(''), respectively) embedded in an FCC substitutional solid solution consisting primarily of Ni and other elements which confer desired properties depending upon the application. The grain size may vary from as small as 2 μm for powder metallurgy alloys used in discs to single crystals the actual size of the component for turbine blades. The fatigue behaviour depends upon the microstructure, deformation mode, environment and cycle time. In many cases, it can be controlled or modified through small changes in composition which may dramatically change the mechanism of damage accumulation and the fatigue life. In this paper, the fundamental microstructural, compositional, environmental and deformation mode factors which affect fatigue behaviour are critically reviewed. Connections are made across a range of studies to provide more insight. Modern approaches are pointed out in which the wealth of available microstructural, deformation and damage information is used for computerized life prediction. The paper ends with a discussion of the very important and highly practical subject of thermo-mechanical fatigue (TMF). It is shown that physics-based modelling leads to significantly improved life prediction. Suggestions are made for moving forward on the critical subject of TMF life prediction in notched components.
منابع مشابه
A Thermomechanical Fatigue Crack Initiation Model for Directionally-solidified Ni-base Superalloys
Nickel-base superalloys have been used extensively in power generation applications due to their high strength at temperatures up to 1093°C. When the material is subjected to complex mechanical loading superimposed with thermal loading, fatigue interacts with either creep and/or oxidation. Directionallysolidified (DS) materials are often used in place of polycrystalline (PC) materials since the...
متن کاملEffect of bonding time on microstructure and mechanical properties during TLP bonding of nickel-base superalloys Hastelloy C276 and Stainless Steel AISI316
Joining of Hastelloy C276 nickel-base superalloy to AISI316 Stainless Steel using BNi-2 interlayer performed by transient liquid phase process (TLP) at 1150°C for 5 and 30 minutes. Bonding microstructure was studied using an Optical microscope and a scanning electron microscope (SEM). Vickers hardness test and shear strength test have been used to evaluate the mechanical properties. Microstruct...
متن کاملEffect of bonding time on microstructure and mechanical properties during TLP bonding of nickel-base superalloys Hastelloy C276 and Stainless Steel AISI316
Joining of Hastelloy C276 nickel-base superalloy to AISI316 Stainless Steel using BNi-2 interlayer performed by transient liquid phase process (TLP) at 1150°C for 5 and 30 minutes. Bonding microstructure was studied using an Optical microscope and a scanning electron microscope (SEM). Vickers hardness test and shear strength test have been used to evaluate the mechanical properties. Microstruct...
متن کاملVacuum Levels Needed to Simulate Internal Fatigue Crack Growth in Titanium Alloys and Nickel-base Superalloys: Thermodynamic Considerations (preprint)
Prior studies have examined fatigue growth of surface cracks in vacuum to simulate sub-surface growth in Ti-alloys and Ni-base superalloys. Even with the highest vacuum level attained using “state-of-the-art” pumps, it is unclear if conditions of internal crack growth are truly simulated. We consider thermodynamics of the oxidation process to help answer this question. This consideration helps ...
متن کاملVacuum Levels Needed to Simulate Internal Fatigue Crack Growth in Titanium Alloys and Nickel-base Superalloys: Thermaodynamic Considerations (preprint)
Prior studies have examined fatigue growth of surface cracks in vacuum to simulate sub-surface growth in Ti-alloys and Ni-base superalloys. Even with the highest vacuum level attained using “state-of-the-art” pumps, it is unclear if conditions of internal crack growth are truly simulated. We consider thermodynamics of the oxidation process to help answer this question. This consideration helps ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Philosophical transactions. Series A, Mathematical, physical, and engineering sciences
دوره 373 2038 شماره
صفحات -
تاریخ انتشار 2015