Direct observation of spinodal decomposition phenomena in InAlN alloys during in-situ STEM heating
نویسندگان
چکیده
The spinodal decomposition and thermal stability of thin In0.72Al0.28N layers and In0.72Al0.28N/AlN superlattices with AlN(0001) templates on Al2O3(0001) substrates was investigated by in-situ heating up to 900 °C. The thermally activated structural and chemical evolution was investigated in both plan-view and cross-sectional geometries by scanning transmission electron microscopy in combination with valence electron energy loss spectroscopy. The plan-view observations demonstrate evidence for spinodal decomposition of metastable In0.72Al0.28N after heating at 600 °C for 1 h. During heating compositional modulations in the range of 2-3 nm-size domains are formed, which coarsen with applied thermal budgets. Cross-sectional observations reveal that spinodal decomposition begin at interfaces and column boundaries, indicating that the spinodal decomposition has a surface-directed component.
منابع مشابه
The immiscibility of InAlN ternary alloy
We have used two models based on the valence force field and the regular solution model to study the immiscibility of InAlN ternary alloy, and have got the spinodal and binodal curves of InAlN. Analyzing the spinodal decomposition curves, we obtain the appropriate concentration region for the epitaxial growth of the InN-AlN pseudobinary alloy. At a temperature most common for the epitaxial grow...
متن کاملTEM Characterization and Properties of Cu-1 wt.% TiB2 Nanocomposite Prepared by Rapid Solidification and Subsequent Heat Treatment
Copper matrix composite reinforced by 1wt.% TiB2 particles was prepared using in situ reaction of Cu-1.4wt.% Ti and Cu-0.7wt.% B by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºC. High-resolution transmission electron microscopy (HRTEM) characterization showed that primary TiB2 particles were formed in liquid copper. Heat treatment of as-solidified samples led to ...
متن کاملSpinodal Decomposition for Multi-component Cahn-hilliard Systems
We consider the initial stage phase separation process in multi-component CahnHilliard systems through spinodal decomposition. Relying on recent work of MaierPaape and Wanner we establish the existence of certain dominating subspaces determining the behavior of most solutions originating near a spatially homogeneous state. It turns out that depending on the initial concentrations of the alloy c...
متن کاملCascades of Spinodal Decompositions in the Ternary Cahn-hilliard Equations
The dynamics of the Cahn-Hilliard equations for a ternary alloy are studied during the phase separation process. The results show a primary spinodal decomposition followed by coarsening and then possibly a secondary spinodal decomposition.
متن کاملTi-alloys: Potential nano-modifier for Rocket Propellants
Composite solid propellants were prepared with and without nano-alloys (Ti-Co, Ti-Ni, Ti-Zn), where nano-alloys used as catalyst. These nano-alloys are prepared by hydrazine reduction method. Catalytic properties of these nanomaterials were measured on Ammonium perchorate/hydroxyterminatedpolybutadiene propellant by thermogravimetery analysis and differential thermal analysis. Both experimental...
متن کامل