A probabilistic method to predict fatigue crack initiation
نویسندگان
چکیده
A probabilistic method to predict macrocrack initiation due to fatigue damage is presented in this paper. Acoustic non-linearity is used to quantify pre-macrocrack initiation damage. This data is then used in a probabilistic analysis of fatigue damage. The probabilistic fatigue damage analysis consists of a suitably chosen damage evolution equation to model accumulated damage coupled with a procedure to calculate the probability of macrocrack initiation. The probability of macrocrack initiation is evaluated using the Monte Carlo Method with Importance Sampling. Numerical results for the probabilistic assessment of fatigue damage for a sample problem are presented and compared with experimental results.
منابع مشابه
Predicting Low Cycle Fatigue Life through Simulation of Crack in Cover Plate Welded Beam to Column Connections
This paper presents a low cycle fatigue life curve by simulating a crack in a cover plate welded moment connection. Initiation of ductile fracture in steel is controlled by growth and coalescence of micro-voids. This research used a numerical method using finite element modeling and simulation of ductile crack initiation by a micromechanical model. Therefore, a finite element model of a cover p...
متن کاملExperimental Investigation and Numerical Prediction of Fatigue Life in Force Fitted Fastener Holes
In this paper, the effect of interference fit on fatigue life of holed plate of mechanical joints was investigated experimentally. Fatigue tests were carried out on the holed specimens of Al-alloy 7075-T6 alloy. The interference fit process consists of force fitting a fastener into the hole with a negative clearance (diameter of the fastener is larger than of the hole) that produces beneficial ...
متن کاملSide Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملEffect of Boundary Condition on Pre-Existing Crack Under Fatigue Loading
In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...
متن کاملEstimation of Maximum Inclusion Size and Fatigue Limit in HSLA-100 Steel
The objective of the current study is to determine the fatigue limit of a clean and high-performance material named as HSLA-100 steel and to compare the obtained fatigue limit with that of theoretically predicted fatigue limit by statistics of extreme value (SEV) method. Also, the size of inclusions located at the site of fatigue crack nucleation on the fracture surface of the fatigue test spec...
متن کامل