Frequency dependence of the magnetoimpedance in amorphous CoP electrodeposited layers
نویسندگان
چکیده
Magnetic properties and changes of impedance upon external field ~MI! are studied in amorphous CoP magnetic layers obtained by galvanostatic electrodeposition over cylindrical Cu substrates. The magnetic layer thickness is controlled by deposition time and varies between 3 and 7 mm. Due to the columnar growth of Co, thicker layers have stronger perpendicular radial anisotropy. The field and frequency dependence of the impedance is measured in the kHz/MHz range. Although it is generally accepted that a radial anisotropy should be unfavorable to the MI effect, an increase of the MI ratio with the thickness of the magnetic layer, and thus with anisotropy, is observed. Results are explained in terms of a model considering the current distribution along the sample thickness with two well-defined regions having different transport and magnetic properties. © 2000 American Institute of Physics. @S0021-8979~00!57108-4#
منابع مشابه
Nonlinear magnetoimpedance and parametric excitation of standing spin waves in a glass-covered microwire
The giant magnetoimpedance of an 8.5 m glass-covered amorphous microwire was investigated in the frequency range of 10 MHz–3.5 GHz. It was found that when the exciting microwave current exceeds some threshold value, a periodic fine structure appears in the frequency dependence of the complex impedance. The appearance of this nonlinear phenomenon is interpreted to be a consequence of the paramet...
متن کاملGamma Irradiation Effect on Asymmetric Giant Magnetoimpedance of Co68.15Fe4.35Si12.5B15 Amorphous Alloy
The giant magneto impedance (GMI) effect is a large variation in the electrical impedance of a magnetic conductor when subjected to a static magnetic field. The sensitivity to the direction (AGMI) and magnitude of applied magnetic field and also linearity levels of this effect are three important parameters in magnetic sensors application. A suitable annealing procedure can be used to ac...
متن کاملEffect of Joule-Heating Annealing on Giant Magnetoimpedance of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1 and 2) Melt-Spun Ribbons
In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...
متن کاملGiant magnetoimpedance and field sensitivity in amorphous and nanocrystalline (Co1â‹TMxFex)89Zr7B4 (xâ•›=â•›0, 0.025, 0.05, 0.1) ribbons
متن کامل
A STUDY ON THE ALUMINIZING OF ELECTRODEPOSITED NICKELAT 500 oC
Abstract: nanocrystalline nickel samples with the grain size of ~25 nm were prepared via direct current electrodeposition andaluminized for different durations by pack cementation method at 500 means of SEM, EDS and XRD techniques. According to results, short time aluminizing resulted in the formation of asingle aluminide layer whereas at long duration two distinct aluminide layers were formed....
متن کامل