Wear Analysis of Second-generation Highly Cross-Linked Polyethylene in Primary Total Hip Arthroplasty.

A major limiting factor in the longevity of total hip replacement is the wear rate of the hip bearing. As manufacturing technology has improved during the past several decades, much attention has been focused on developing newer generations of polyethylene that have lower rates of wear while minimizing free radical formation and subsequent osteolysis. The turning point for the manufacture of polyethylene was moving from gamma irradiation in air to irradiation in a low oxygen environment, which reduced free radical formation while increasing the wear resistance. New polyethylene manufacturing methods, including multiple cycles of irradiation and annealing, have resulted in greater wear resistance. Wear analysis studies are essential to determine if these new liners actually show a benefit from prior generations of polyethylene and, more importantly, if they are safe to use. This study involved a single center retrospective review of 60 patients with a mean follow-up of 5.5 years who underwent primary total hip arthroplasty with a second-generation highly cross-linked polyethylene manufactured by 3 cycles of sequential irradiation and annealing. Linear and volumetric wear rates were determined from digitized radiographs using contemporary wear analysis software. The mean linear wear rate for the entire group was 0.025 millimeters per year (mm/y). This value represents a linear wear rate 2.7 times less than that of a first-generation highly cross-linked polyethylene and 4.2 times less than that of a conventional polyethylene. At an average of 5 years, compared with a first-generation highly cross-linked polyethylene, a second-generation highly cross-linked polyethylene appears to show significant improvement regarding wear. [Orthopedics. 2016; 39(6):e1178-e1182.].