Manipulation of Optical Transmittance by Ordered-Oxygen-Vacancy in Epitaxial LaBaCo2O5.5+δ Thin Films
نویسندگان
چکیده
Giant optical transmittance changes of over 300% in wide wavelength range from 500 nm to 2500 nm were observed in LaBaCo2O5.5+δ thin films annealed in air and ethanol ambient, respectively. The reduction process induces high density of ordered oxygen vacancies and the formation of LaBaCo2O5.5 (δ = 0) structure evidenced by aberration-corrected transmission electron microscopy. Moreover, the first-principles calculations reveal the origin and mechanism of optical transmittance enhancement in LaBaCo2O5.5 (δ = 0), which exhibits quite different energy band structure compared to that of LaBaCo2O6 (δ = 0.5). The discrepancy of energy band structure was thought to be the direct reason for the enhancement of optical transmission in reducing ambient. Hence, LaBaCo2O5.5+δ thin films show great prospect for applications on optical gas sensors in reducing/oxidizing atmosphere.
منابع مشابه
Anisotropic Strain Induced Directional Metallicity in Highly Epitaxial LaBaCo2O5.5+δ Thin Films on (110) NdGaO3
Highly directional-dependent metal-insulator transition is observed in epitaxial double perovskite LaBaCo2O5.5+δ films. The film exhibit metallic along [100], but remain semiconducting along [010] under application of a magnetic field parallel to the surface of the film. The physical origin for the properties is identified as in-plane tensile strain arising from oxygen vacancies. First-principl...
متن کاملUltraviolet detectors based on annealed zinc oxide thin films: epitaxial growth and physical characterizations
In this report, ultraviolet (UV) detectors were fabricated based on zinc oxide thin films. The epitaxial growth of zinc oxide thin films was carried out on bare glass substrate with preferred orientation to (002) plane of wurtzite structure through radio frequency sputtering technique. The structural properties indicated a dominant peak at 2θ=34.28º which was matched with JCPDS reference card N...
متن کاملGas Sensing Properties of Epitaxial LaBaCo2O5.5+δ Thin Films
Chemical reactivity and stability of highly epitaxial mixed-conductive LaBaCo2O5.5+δ (LBCO) thin films on (001) LaAlO3 (LAO) single-crystalline substrates, fabricated by using pulsed laser deposition system, were systematically investigated. Microstructure studies from x-ray diffraction indicate that the films are c-axis oriented with the interface relationship of [100]LBCO//[100]LAO and (001)L...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کامل