Simulations reveal the role of composition into the atomic-level flexibility of bioactive glass cements.
نویسندگان
چکیده
Bioactive glass ionomer cements (GICs), the reaction product of a fluoro-alumino-silicate glass and polyacrylic acid, have been in effective use in dentistry for over 40 years and more recently in orthopaedics and medical implantation. Their desirable properties have affirmed GIC's place in the medical materials community, yet are limited to non-load bearing applications due to the brittle nature of the hardened composite cement, thought to arise from the glass component and the interfaces it forms. Towards helping resolve the fundamental bases of the mechanical shortcomings of GICs, we report the 1st ever computational models of a GIC-relevant component. Ab initio molecular dynamics simulations were employed to generate and characterise three fluoro-alumino-silicate glasses of differing compositions with focus on resolving the atomic scale structural and dynamic contributions of aluminium, phosphorous and fluorine. Analyses of the glasses revealed rising F-content leading to the expansion of the glass network, compression of Al-F bonding, angular constraint at Al-pivots, localisation of alumino-phosphates and increased fluorine diffusion. Together, these changes to the structure, speciation and dynamics with raised fluorine content impart an overall rigidifying effect on the glass network, and suggest a predisposition to atomic-level inflexibility, which could manifest in the ionomer cements they form.
منابع مشابه
Comparison of the solubility of three resin cements and a resin-modified glass ionomer cement: An in vitro study
Background and aims: Solubility is an important property of luting cements in determining clinical durability. The aim of this study was to compare the solubility of Panavia, Calibra and Maxcem resin cements with that of GC Fuji PLUS resin modified glass ionomer cement in three different pH values. Materials and Methods: A total of 96 specimens were prepared (8mm diameter, 4mm thickness) accor...
متن کاملتهیه، مشخصهیابی و ارزیابی مقایسهای زیست فعالی سه نوع نانو پودر شیشه زیست فعال برای کاربردهای پزشکی
Fabrication of biomaterials with ability to form a bond with bone tissue for bone skeletal system repair is one of the biomaterial science aims. Bioactive glasses containing CaO-SiO2-P2O5 are among the most important groups used in biomedicine and dentistry such as bone defect repair and maxillo-facial reconstruction. The aim of this work was preparation and characterization of nano particle b...
متن کاملIn-vitro Comparison of the Antimicrobial Properties of Glass Ionomer Cements with Zinc Phosphate Cements
White spot lesions are observed in nearly 50% of patients undergoing orthodontic treatment. Long-lasting antibacterial properties of orthodontic cements can reduce this phenomenon. The aim of this research was to compare antimicrobial activity of three commercial glass ionomer cements with three commercial zinc phosphate cements, over time, against streptococcus mutans and candida albicans...
متن کاملStructure of bioactive glass and its application to glass ionomer cement.
We prepared a new glass ionomer cement using bioactive CaO-P2O5-SiO2(-MgO) glass and investigated its setting process using FT-IR and MAS NMR analyses. The compressive strengths of the cements depended on the glass composition and a maximum strength of 33.3 +/- 4.7 MPa was obtained using cement with the glass composition of MgO:4.6, CaO:44.9, SiO2:34.2 and P2O5:16.3% in weight. FT-IR analysis s...
متن کاملComparative Evaluation of the Remineralizing Effects and Surface Microhardness of Glass Ionomer Cements
Glass ionomer cements (GICs) are widely used in restorative dentistry.1 In dentistry, one of their advantages over other restorative materials is that they can be placed into tooth cavities without an additional bonding agent.2 They also possess a fluoride-releasing property3 and are relatively biocompatible with the pulp.1 Adhesive property and fluoride release of glass ionomer cement contribu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Physical chemistry chemical physics : PCCP
دوره 18 2 شماره
صفحات -
تاریخ انتشار 2016