Superconducting phase formation in random neck syntheses: a study of the Y-Ba-Cu-O system by magneto-optics and magnetometry
نویسنده
چکیده
Magneto-optical imaging and magnetization measurements were applied to investigate local formation of superconducting phase effected by a random neck synthesis in Y-Ba-Cu-O system. Polished pellets of strongly inhomogeneous ceramic samples show clearly the appearance of superconducting material in the intergrain zones of binary primary particles reacted under different conditions. Susceptibility measurements allows evaluation of superconducting critical temperature, which turned out to be close to that of optimally doped YBa2Cu3O7−x.
منابع مشابه
بررسی ابررسانای Bi1.6Pb0.4Sr2-xBaxCa2Cu3Oy ساخته شده به روش سل- ژل
In this study, the effect of Ba substitution for Sr in the Bi-Pb-Sr-Ca-Cu-O (BPSCCO) system was investigated. The Bi1.6Pb0.4Sr2-xBaxCa2Cu3Oy superconductor with 0.0, 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 at annealing times of 16, 32, 48 and 64 hour was made by the sol-gel method. In order to study the microstructure of samples, SEM images and X-ray diffraction (XRD) was performed. The crystal la...
متن کاملتأثیر نانوپودر آلومینا بر تشکیل فاز و ویژگیهای ابررسانایی Bi1.6Pb0.4Sr1.9Ca2.1Cu3O10-y
In this work Bi1.6Pb0.4Sr1.9Ca2.1Cu3O10-y superconducting system (Bi2223) has been prepared by solid state reaction and the effect of nanoalumina additive on the phase formation and supercoducting properties have been investigated. XRD investigations show that addition of 0.2 wt% of nanoalumina on the superconducting system improved Bi-2223 phase formation . The results show that Jc increases...
متن کاملComposition of Pulsed-Laser-Deposited Y-Ba-Cu-O and Ba-K-Bi-O Thin Films
The composition of pulsed-laser-deposited Y-Ba-Cu-O and Ba-K-Bi-O thin films is shown to be strongly affected by target conditioning, gas pressure, and targetsubstrate distance. For both compounds, ablation from a freshly sanded target surface results in films with an excess of the more volatile elements. The concentration of these volatile elements in the films decreases until the system reach...
متن کاملSuperconducting and structural properties of plasma sprayed Y-Ba-Cu-O layers deposited on metallic substrates*
The properties of plasma sprayed Y-Ba-Cu-O coatings deposited on metallic substrates are studied. Stainless steel, nickel steels and pure nickel are used as substrate. Y-Ba-Cu-O deposited on stainless steel and nickel steel reacts with the substrate. This interaction can be suppressed by using an yttria-stabilized zirconia (YsZ) diffusion barrier. However, after heat treatment the Y-Ba-Cu-O lay...
متن کامل