Nanoparticle-reinforced resin-based dental composites.

نویسندگان

  • Yang Xia
  • Feimin Zhang
  • Haifeng Xie
  • Ning Gu
چکیده

OBJECTIVE TiO(2) nanoparticles treated with the organosilane allyltriethoxysilane (ATES) are used to improve the mechanical properties of dental resin-based composites (RBCs, Z100, 3M ESPE). METHODS TiO(2) nanoparticles were sonically dispersed in an ethanol solution containing ATES. The modified particles were washed in pure ethanol and dried before being used as filler. Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM) were used to analyze the nanoparticles. Five groups of composite resin specimens were prepared: one control group, and four groups using either modified or unmodified nanoparticles comprising 0.5% or 1.0% of the material by weight. The mechanical properties (microhardness and flexural strength) of all five groups of specimens were measured. RESULTS After modification, the particles' FTIR spectrum shows a new absorption doublet at 1200 and 1020 cm(-1). TEM images show that the modified particles have better dispersion, and that their clusters are small enough to create a homogeneous surface on dental RBCs. Composite resin specimens including modified nano-TiO(2) have significantly better mechanical properties than the control group (P<0.05). The improvement of adding 1.0 wt.% modified nano-TiO(2) particles was better than that of 0.5 wt.%. CONCLUSIONS Surface modification by the organosilane ATES influences the dispersion and linkage of TiO(2) nanoparticles within a resin matrix, and the modified particles are found to improve the microhardness and flexural strength of dental RBCs.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Micromechanical analysis of nanoparticle-reinforced dental composites

The mechanical behavior of TiO2 nanoparticle-reinforced resin-based dental composites was characterized in this work using a three-dimensional nanoscale representative volume element. The impacts of nanoparticle volume fraction, aspect ratio, stiffness, and interphase zone between the resin matrix and nanoparticle on the bulk properties of the composite were characterized. Results clearly demon...

متن کامل

STRENGTH AND FRACTURE TOUGHNESS OF WHISKER REINFORCED DENTAL RESIN-BASED COMPOSITES

Enhancing the properties of dental resin composites is of interest to researchers. The objective of the present investigation was to improve the strength and fracture toughness of dental composites via addition of silicon carbide whiskers and substitution of commonly used filler materials with stabilized zirconia ceramic powder. It was also intended to study the effect of powder- to- whisker ra...

متن کامل

High Elastic Modulus Nanopowder Reinforced Resin Composites for Dental Applications

Title of dissertation: HIGH ELASTIC MODULUS NANOPOWDER REINFORCED RESIN COMPOSITES FOR DENTAL APPLICATIONS Yijun Wang, Doctor of Philosophy, 2007 Dissertation directed by: Associate Professor Isabel K. Lloyd Department of Material Science and Engineering Dental restorations account for more than $3 billion dollars a year on the market. Among them, all-ceramic dental crowns draw more and more at...

متن کامل

Ceramic whisker reinforcement of dental resin composites.

Resin composites currently available are not suitable for use as large stress-bearing posterior restorations involving cusps due to their tendencies toward excessive fracture and wear. The glass fillers in composites provide only limited reinforcement because of the brittleness and low strength of glass. The aim of the present study was to reinforce dental resins with ceramic single-crystalline...

متن کامل

Effects of fibers on the color change and stability of resin composites after accelerated aging.

Composite resins were reinforced with glass and polyethylene fibers in this study, and the effect of fiber reinforcement on the color change of composite resins was investigated. After accelerated aging, the effect of fiber reinforcement on the color stability of composite resins was also examined. There were three experimental groups (n=12 disks per group): non-fiber-reinforced composite (non-...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Journal of dentistry

دوره 36 6  شماره 

صفحات  -

تاریخ انتشار 2008