Study on Charge Distribution of Carboxymethylated Cotton Fabric by Streaming Potential/Current Measurements
نویسندگان
چکیده
Carboxymethylated cotton might provide an eco-friendly novel approach to impart different functions to fabric by crosslinking or self-assembly deposition of nanolayers. The anionic content of carboxymethylated cotton was determined by acid-base titration. Two interrelated methods of surface electrochemistry for anionic cotton fabrics were investigated in this paper. Measurement of surface charge on carboxymethylated cotton was achieved by characterizing the zeta potential of the anionized fibers via streaming current (SC) and fiber-pad streaming potential (SP) measurements, which showed only a small percentage of total charges contributed to the surface charge. SC and SP methods were proven to be useful in studying the surface charge of ionic cellulose. Key Terms Carboxymethylated Cotton, Streaming Current, Streaming Potential, Surface Charges, Total Charges
منابع مشابه
Microwave Assisted Appraisal of Neem Bark Based Tannin Natural Dye and its Application onto Bio-mordanted Cotton Fabric
The current study is aimed to utilize the microwave for isolation of colorant from neem bark and its application onto chemical & bio-mordanted cotton fabric. For the purpose, aqueous, acid and organic media have been employed to isolate the colorant and to make its application onto surface modified and bio-mordanted cotton fabric followed by microwave treatment up to 6min....
متن کاملInk-Jet Printing Cotton with Cationic Reactive Dye Based Inks
The current commercial application of ink-jet reactive inks to cotton fabrics has been through pre-treating with pad liquor prior to printing. In This study made an effort to provide a single phase ink-jet printing process for printing cotton fabric using the novel cationic reactive dye in ink’s formulation. Cotton fabric was printed upon with the novel cationic reactive dye and commercial anio...
متن کاملEffect of Fluorination Treatment on Cotton Wettability, Dyeability and Mechanical Properties and Characterization of Surface Changes by XPS
Cotton fabric was treated with fluorine gas in a nitrogen atmosphere. The effect of fluorination treatments on wettability, whiteness index, dyeability and mechanical properties of cotton fabrics were assessed. Kawabata analysis shows that fluorination treatment increases shear stiffness G, shear hysteresis 2HG5, bending stiffness B and overall fabric stiffness Koshi on cotton fabric. Fluorinat...
متن کاملDyeing of Cotton Fabric with Natural Dyes Improved by Mordants and Plasma Treatment
Nowadays, there is a great tendency for eco-dyeing and finishing of textiles with natural products. several natural dyes have been used for dyeing of protein fibers but a low number have the ability to dye cotton fiber because of low affinity of cellulose to the natural dyes. In this study madder and weld natural colorants were used to dye cotton fabric premordanted with three metallic salt...
متن کاملHot Mercerizing of Cotton/Polyester Blend Fabric Effect of Alkali Treatment Temperature on Ttensile Properties , Weight Loss and Shrinkage of Fabric
The presence of defects in cold mercerizing of cotton goods led to the creation of a new method, called hot mercerizing in which caustic soda solution is used at a high temperature. Hot mercerizing is successfully used in cotton blended with some other fibers. In cotton/polyester blend fabrics, this treatment serves a dual purpose: subjectively, it imparts a silklike soft handle to the po...
متن کامل