Sintered Materials Based on Copper and Alumina Powders Synthesized by a Novel Method
نویسندگان
چکیده
منابع مشابه
Combustion-aminolysis synthesis and characterization of CrN/Cu composites
CrN/Cu composite powders were synthesized by employing a novel two-step technique. Firstly, the Cr2O3+CuO precursors were prepared by the solution combustion synthesis (SCS) method using cupric nitrate, urea, and chromium nitrate as initial materials. Subsequently, the SCS precursors were calcined at 850 °C in NH3 for 6 h, and transformed to CrN/Cu composite powders. The composite powders consi...
متن کاملPREPARATION AND SINTERING OF W-20%Wt Cu COMPOSITE POWDERS PRODUCED BY CO-PRECIPITATION METHOD
Abstract: materials can be fabricated by sintering of W-Cu composite powders. In this research W-20%wt Cu composite powderswas synthesized via a co-precipitation method. Precipitate obtained from a mixture of copper nitrate and ammoniumparatungstate (APT) in distilled water contained W-Cu compounds. This precipitate was washed, dried and calcinedat 550 of dried precipitate powder was determined...
متن کاملEffect of Calcination Temperature on the Alumina-Zirconia Nanostructures Prepared by Combustion Synthesis
In this research, a sol gel autocaombustion route has been proposed to synthesize alumina-zirconia composite powders, using ammonium bicarbonate as a new fuel. Then the effect of calcination temperature on phase transformation and crystallite sizes was investigated. To characterize the products XRD, TEM and BET analyses were used. XRD patterns of as-synthesized powder and calcined powders at 11...
متن کاملSynthesis and Characterization of Silver/Alumina Powders
In this research, synthesis and characterization of silver/alumina composite powders was investigated. This kind of metal/ceramic composite powders is used for fabrication of cutting tools inserts. The role of silver is toughening the final product. The powders were synthesized via co-precipitation method. The composition of the synthesized powders was Ag/80% wt 〖Al〗_2 O_3. Silver nitrate, alum...
متن کاملSintering of Al2O3–Ceo2nanopowder Prepared by Co-Precipitation Method
In the present work, Al2O3-CeO2 composite nanopowders were synthesized via co-precipitation method. The sinterability of the synthesized powders was investigated. The results showed that the transformation of transition phases of alumina to α-Al2O3 takes place at 1200 °C. TEM images showed that the powders was composed of nanoparticles in the range of 30−70 nm. The densification of composites s...