Damage Patterns at the Head-Stem Taper Junction Helps Understand the Mechanisms of Material Loss.

نویسندگان

  • Harry S Hothi
  • Andreas C Panagiotopoulos
  • Robert K Whittaker
  • Paul J Bills
  • Rebecca A McMillan
  • John A Skinner
  • Alister J Hart
چکیده

BACKGROUND Material loss at the taper junction of metal-on-metal total hip arthroplasties has been implicated in their early failure. The mechanisms of material loss are not fully understood; analysis of the patterns of damage at the taper can help us better understand why material loss occurs at this junction. METHODS We mapped the patterns of material loss in a series of 155 metal-on-metal total hip arthroplasties received at our center by scanning the taper surface using a roundness-measuring machine. We examined these material loss maps to develop a 5-tier classification system based on visual differences between different patterns. We correlated these patterns to surgical, implant, and patient factors known to be important for head-stem taper damage. RESULTS We found that 63 implants had "minimal damage" at the taper (material loss <1 mm3), and the remaining 92 implants could be categorized by 4 distinct patterns of taper material loss. We found that (1) head diameter and (2) time to revision were key significant variables separating the groups. CONCLUSION These material loss maps allow us to suggest different mechanisms that dominate the cause of the material loss in each pattern: (1) corrosion, (2) mechanically assisted corrosion, or (3) intraoperative damage or poor size tolerances leading to toggling of trunnion in taper.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Method for characterization of material loss from modular head-stem taper surfaces of hip replacement devices

Assessment of the head-stem taper junction requires the estimation of material loss from the taper surfaces of both femoral head and stem. This paper describes a method for the measurement and analysis of material loss from the modular taper junction of hip replacements, in particular femoral stem tapers where generally the entire taper surface has been engaged. In such cases no direct unengage...

متن کامل

Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design

OBJECTIVES The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromi...

متن کامل

Material loss at the taper junction of retrieved large head metal-on-metal total hip replacements.

It has been speculated that material loss, either as corrosion or wear, at the head-stem taper junction is implicated in the high revision rates reported for metal-on-metal total hip replacements. We measured the volume of material loss from the taper and bearing surfaces of retrieved devices, and investigated the associations with blood metal ion levels and the diagnosis of a cystic or solid p...

متن کامل

Assessing the material loss of the modular taper interface in retrieved metal on metal hip replacements

Measuring the amount of material loss in the case of revised hip replacements is considered to be a prerequisite of understanding and assessing the true in vivo performance of the implant. This paper outlines a method developed by the authors for quantifying taper material loss as well as more general taper interface parameters. Previous studies have mostly relied on visual inspection to assess...

متن کامل

Clinically insignificant trunnionosis in large-diameter metal-on-polyethylene total hip arthroplasty

OBJECTIVES Mechanical wear and corrosion at the head-stem junction of total hip arthroplasties (THAs) (trunnionosis) have been implicated in their early revision, most commonly in metal-on-metal (MOM) hips. We can isolate the role of the head-stem junction as the predominant source of metal release by investigating non-MOM hips; this can help to identify clinically significant volumes of materi...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • The Journal of arthroplasty

دوره 32 1  شماره 

صفحات  -

تاریخ انتشار 2017