SiC surface orientation and Si loss rate effects on epitaxial graphene
نویسندگان
چکیده
We have explored the properties of SiC-based epitaxial graphene grown in a cold wall UHV chamber. The effects of the SiC surface orientation and silicon loss rate were investigated by comparing the characteristics of each formed graphene. Graphene was grown by thermal decomposition on both the silicon (0001) and carbon (000-1) faces of on-axis semi-insulating 6H-SiC with a "face-down" and "face-up" orientations. The thermal gradient, in relation to the silicon flux from the surface, was towards the surface and away from the surface, respectively, in the two configurations. Raman results indicate the disorder characteristics represented by ID/IG down to < 0.02 in Si-face samples and < 0.05 in C-faces over the 1 cm2 wafer surface grown at 1,450°C. AFM examination shows a better morphology in face-down surfaces. This study suggests that the optimum configuration slows the thermal decomposition and allows the graphene to form near the equilibrium. The Si-face-down orientation (in opposition to the temperature gradient) results in a better combination of low disorder ratio, ID/IG, and smooth surface morphology. Mobility of Si-face-down orientation has been measured as high as approximately 1,500 cm2/Vs at room temperature. Additionally, the field effect transistors have been fabricated on both Si-face-down and C-face-down showing an ambipolar behavior with more favorable electron conduction.
منابع مشابه
Micro-Raman and micro-transmission imaging of epitaxial graphene grown on the Si and C faces of 6H-SiC
Micro-Raman and micro-transmission imaging experiments have been done on epitaxial graphene grown on the C- and Si-faces of on-axis 6H-SiC substrates. On the C-face it is shown that the SiC sublimation process results in the growth of long and isolated graphene ribbons (up to 600 μm) that are strain-relaxed and lightly p-type doped. In this case, combining the results of micro-Raman spectroscop...
متن کاملInvestigation of structural and electronic properties of epitaxial graphene on 3C–SiC(100)/Si(100) substrates
Graphene has been intensively studied in recent years in order to take advantage of its unique properties. Its synthesis on SiC substrates by solid-state graphitization appears a suitable option for graphene-based electronics. However, before developing devices based on epitaxial graphene, it is desirable to understand and finely control the synthesis of material with the most promising propert...
متن کاملThe effect of doping Graphene Quantum Dots with K, B, N, and Cl on its emitted spectrum
In this work, the effect of doping Graphene Quantum Dots (GQDs) on their emission spectra has been studied. First, graphene has been deposited on SiC substrate by using sublimation method. Second, doped-GQDs have been distributed on the surface of graphene via drop casting. The structure of the samples have been studied and characterized by X-ray diffraction (XRD), Scanning Electron Microscopy ...
متن کاملSurface Chemistry Involved in Epitaxy of Graphene on 3C-SiC(111)/Si(111)
Surface chemistry involved in the epitaxy of graphene by sublimating Si atoms from the surface of epitaxial 3C-SiC(111) thin films on Si(111) has been studied. The change in the surface composition during graphene epitaxy is monitored by in situ temperature-programmed desorption spectroscopy using deuterium as a probe (D(2)-TPD) and complementarily by ex situ Raman and C1s core-level spectrosco...