Argon-shielded hot pressing of titanium alloy (Ti6Al4V) powders.

نویسندگان

  • Zbigniew Gronostajski
  • P Bandoła
  • T Skubiszewski
چکیده

The paper presents the method of the argon - shielded hot pressing of titanium alloy (Ti6A14V) powder (used in medical industry). The powders produced in the GA (gas atomization) process and in the HDH (hydride - dehydride) process were used in the experiments. A pressing process was conducted at a temperature of 800-850 degrees C for different lengths of time. An unoxidized sintered material, nearly as dense as a solid material and having a lamellar structure (alpha+beta), was obtained from the titanium alloy powder produced in the HDH process.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Sintering Properties of Mechanically Alloyed Ti-5Al-2.5Fe

In this study, Ti-5Al-2.5Fe alloy was prepared by powder metallurgy. The elemental titanium, aluminum, and iron powders were mechanically alloyed for 10 h in a vacuum atmosphere. A stainless steel jar and stainless steel balls were used for mechanical alloying. The alloyed powders were then sintered by vacuum hot pressing at 950 °C for a soaking time of 30 minutes. Pure titanium was also sinter...

متن کامل

Controllable two-scale network architecture and enhanced mechanical properties of (Ti5Si3+TiBw)/Ti6Al4V composites

Novel Ti6Al4V alloy matrix composites with a controllable two-scale network architecture were successfully fabricated by reaction hot pressing (RHP). TiB whiskers (TiBw) were in-situ synthesized around the Ti6Al4V matrix particles, and formed the first-scale network structure (FSNS). Ti5Si3 needles (Ti5Si3) precipitated in the β phase around the equiaxed α phase, and formed the secondary-scale ...

متن کامل

Characterization of loose powder sintered porous titanium and Ti6Al4V alloy

Porous titanium and Ti6Al4V alloy, biomedical candidate materials for use in orthopedic and dental implants, were manufactured by sintering the powders at various temperatures in loose condition. The characteristics of the corresponding powders and utilized sintering temperatures limited the final porosities in the range 30-37.5 vol. %. Similar to wrought alloys, compression stress-strain curve...

متن کامل

Effect of CeO2 on Microstructure and Wear Resistance of TiC Bioinert Coatings on Ti6Al4V Alloy by Laser Cladding

To solve the lack of wear resistance of titanium alloys for use in biological applications, various prepared coatings on titanium alloys are often used as wear-resistant materials. In this paper, TiC bioinert coatings were fabricated on Ti6Al4V by laser cladding using mixed TiC and ZrO₂ powders as the basic pre-placed materials. A certain amount of CeO₂ powder was also added to the pre-placed p...

متن کامل

Mechanical properties and microstructural evolution of vacuum hot-pressed titanium and Ti-6Al-7Nb alloy.

Hot-pressing is a powder metallurgy process where loose powder is loaded into a mould, usually of graphite, and sintered by the simultaneous application of high temperature and pressure. In this study elemental titanium and Ti-6Al-7Nb alloy powders are hot-pressed under different conditions in order to study the influence of the processing parameters on the microstructure and mechanical propert...

متن کامل

ذخیره در منابع من

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Acta of bioengineering and biomechanics

دوره 12 1  شماره 

صفحات  -

تاریخ انتشار 2010