Elasticity, Stability and Ideal Strength of β-SiC in plane-wave-based ab initio calculations

On the basis of the pseudopotential plane-wave(PP-PW) method and the local-density-functional theory(LDFT), this paper studies energetics, stressstrain relation, stability and ideal strength of β-SiC under various loading modes, where uniform uniaxial extension and tension, biaxial proportional extension are considered along directions [001] and [111]. The lattice constant, elastic constants and moduli of equilibrium state are calculated, and the results agree well with the experimental data. As the four Si-C bonds along directions [111], [111], [111] and [111] are not the same under the loading along [111], internal relaxation and the corresponding internal displacements must be considered. We find that, at the beginning of loading, the effect of internal displacement through shuffle and glide plane diminishes the difference among the four Si-C bonds length, but will increase the difference at the subsequent loading, which will result in a crack nucleated on {111} shuffle plane and a subsequently cleavage fracture. Thus the corresponding theoretical strength is 50.8 GPa, which agrees well with the recent experiment value, 53.4 GPa. However, with the loading along [001], internal relaxation is not important for tetragonal symmetry. Elastic constants during the uniaxial tension along [001] are calculated. Based on the stability analysis with stiffness coefficients, we find that the spinodal and Born instabilities are triggered almost at the