Effects of Stoichiometry on the Magnetic and Structural Properties of Perpendicular Barium Ferrite Thin Film Media
نویسندگان
چکیده
The effects of stoichiometry factor on the magnetic and structural properties of perpendicular barium ferrite thin films with composition of BaO (Fe2O3) were systematically investigated. Within the range 2 2 6, the -axis for barium ferrite thin films can be oriented perpendicularly by the use of Pt underlayer and with optimized processing conditions. Perpendicular -axis orientation becomes worse as decreases from 6 to 2.2. The average grain size was greatly reduced from about 2000 Å to 300 Å with the decrease of . The decrease of the grain size can be related to the existence of nonmagnetic phase BaFe2O4, which was observed by X-ray diffraction.
منابع مشابه
ساخت و بررسی نمونههای حجمی و لایه نازک فریت استرانسیوم
In this article, bulk and thin film samples of strontium ferrite have been studied. Due to the high electrical resistivity in strontium ferrite, energy loss due to eddy currents reduces and because of this, it can be used in high frequency magnetic circuits. On the other hand, strontium ferrite has attracted much attention as a permanent magnet. At first, we study the preparation process of b...
متن کاملBarium and Strontium Ferrite Perpendicular Thin Film Media with a Sendust Soft Magnetic Underlayer
The possibility of using sendust (FeAlSi) as the soft magnetic underlayer for hexagonal barium ferrite (BaM) and strontium ferrite (SrM) was studied. Sendust films were found to retain their soft magnetic properties with a rapid thermal anneal (RTA) at 800 C for 60 s, which is necessary to crystallize the as-deposited amorphous BaM and SrM films. Several film structures with sendust films as th...
متن کاملBarium ferrite thin film media with perpendicular c-axis orientation and small grain size
Barium ferrite thin films with perpendicular c-axis orientation and small grain size ~about 300 Å! were successfully fabricated with careful control of sputtering conditions. The c-axis orientation of barium ferrite thin films is most sensitive to the oxygen partial pressure during deposition. All samples with oxygen gas during deposition have a random c-axis texture, as indicated by existence ...
متن کاملThin films of barium ferrite with perpendicular magnetic anisotropy produced by laser ablation deposition
Barium ferrite thin films with perpendicular magnetic anisotropy have been prepared on heated (001) sapphire substrates by laser ablation deposition in an oxygen atmosphere using a KrF excimer laser. X-ray diffraction patterns reveal highly oriented films of the magnetoplumbite phase with a c-axis angular spread of 1.8”. Scanning electron micrographs reveal that these films are polycrystalline ...
متن کاملpH and Properties of Synthesized Barium Hexa-Ferrite by Co-precipitation Method
Synthesis of BaFe12O19 magnetic nano particles via precipitation in different pH conditions have been reported. The certain molar ratio of Fe/Ba = 12 selected and sodium hydroxide was used as a precipitant agent. X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and vibrating sample magnetometer (VSM) were used to consider the structural, morphological and magnetic properties of bariu...