Molybdenum targets produced by mechanical reshaping
نویسندگان
چکیده
Targets required to determine the parameters of the 100Mo(p,xn)99mTc reaction and to estimate the yield of the 99mTc production were prepared starting with powder material. Material, melted with electron beam gun into solid bead, was reshaped into foil mechanically. Targets were prepared by powder melting and hot flattening of the droplet followed by cold rolling. Procedure allowed preparation of thick (in the range of hundreds of microns) and thin (down to 250 nm) foils.
منابع مشابه
Analysis of Roll Wear in Reshaping Using Finite Element Simulation
Reshaping process is a widely used method for producing tubes with non-circular cross sections. Owing to the friction between pipe and rolls, initial round pipe moves forward and consequently, it gradually formed into square or rectangular one. In practice, geometric profile of the rolls will be changed after a while. These changes would be detrimental the production of faultless products. Ther...
متن کاملSynthesis and Characterization of Nanocrystalline Ni50Al50-xMox (X=0-5) Intermetallic Compound During Mechanical Alloying Process
In the present study, nanocrystalline Ni50Al50-xMox (X = 0, 0.5, 1, 2.5, 5) intermetallic compound was produced through mechanical alloying of nickel, aluminum, and molybdenum powders. AlNi compounds with good and attractive properties such as high melting point, high strength to weight ratio and high corrosion resistance especially at high temperatures have attracted the attention of many rese...
متن کاملHydrogen evolution activity of NiMo-MoO2 produced by mechanical milling
In this study, mechanical alloying was done by a high-energy planetary ball milling technique. A mixture of NiO and MoO3 and graphite powders were used as initial materials. After milling of powder mixture with 40 wt.% additional graphite, a temperature of 400, 550 and 1000 °C for 1 h was considered for the heat treatment of powder mixture. Also, powder mixtures containing 60, 80 and 100 wt.% a...
متن کاملAssessment of molybdenum breakthrough levels in molybdenum-99/technetium-99m generators: One year experience at NIMRA Jamshoro Pakistan
Background: Technetium-99m radioisotope is the backbone of any nuclear medicine institute. This radioisotope is acquired by the elution of Molybdenum-99/Technetium-99m generator which emits 141 keV gamma ray and having 6.04 hour half-life. Occasionally the contents of Molybdenum-99 may mix up with elute, which may affect image quality and patients may receive higher doses than recommended. This...
متن کاملStatistical Analysis and Optimization of the Yield Strength and Hardness of Surface Composite Al7075/Al2O3 Produced by FSP via RSM and Desirability Approach
In order to improve the properties of aluminum and its alloys, some various approaches (e.g. reduction of grain size, addition of alloying elements and composite manufacturing) have been considered. Among all these processes, the use of solid-state processes such as the friction stir processing (FSP) is highly convenient to create surface composites at temperatures below the melting point. Ther...
متن کامل